Abstract:Layered Li-rich, Fe- and Mn-based cathode material, Li[Li0.2Fe0.1Ni0.15Mn0.55]O2, has been successfully synthesized by a coprecipitation method and further modified with different coating amounts of AlPO4 (3, 5, and 7 wt %). The effects of AlPO4 coating on the structure, morphology and electrochemical properties of these materials are investigated systematically. XRD results show that the pristine sample is obtained with typical Li-rich layered structure and trace amount of Li3PO4 phase are observed for the coated samples. The morphology observations reveal that all the samples show spherical particles (3-4 μm in diameter) with hierarchical structure, composed of nanoplates and nanoparticles. XPS analysis confirms the existence of AlPO4 and Li3PO4 phases at the surface. The electrochemical performance results indicate that the sample coated with 5 wt % AlPO4 exhibits the highest reversible capacity (220.4 mA h g(-1) after 50 cycles at 0.1C), best cycling performance (capacity retention of 74.4% after 50 cycles at 0.1C) and rate capability (175.3 mA h g(-1) at 1C, and 120.2 mA h g(-1) at 10C after 100 cycles) among all the samples. Cycle voltammograms show good reversibility of the coated samples. EIS analysis reveals that charge transfer resistance after coating is much lower than that of the pristine sample. The excellent electrochemical performances can be attributed to the effects of multifunctional AlPO4 coating layer, including the suppression of surface side reaction and oxygen vacancies diffusion, the acceleration of lithium ions transport as well as the lower electrochemical resistance. Our research provides a new insight of surface modification on low-cost Li-rich material to achieve high energy as the next-generation cathode of lithium-ion batteries.

Structure and Electrochemical Performance of LiFePO4/C Cathode Materials Coated with Nano Al2O3 for Lithium-ion Battery

Structure and Electrochemical Performance of LiFePO_4/C Cathode Materials Coated with Nano Al_2O_3for Lithium-ion Battery

Enhanced Electrochemical Performance of LiNi0.8Co0.15Al0.05O2 Cathode Material via Li2TiO3 Nanoparticles Coating

Enhanced Electrochemical Performance of Li2FeSiO4/C Cathode Materials by Surface Modification with AlPO4 Nanosheets

Enhanced electrochemical properties of Al2O3-coated LiNiPO4 cathode materials for lithium-ion batteries

Surface Structure Investigation of Lini0.8co0.2o2 by Alpo4 Coating and Using Functional Electrolyte

Multifunctional AlPO4 Coating for Improving Electrochemical Properties of Low-Cost Li[Li0.2Fe0.1Ni0.15Mn0.55]O2 Cathode Materials for Lithium-Ion Batteries.

Electrochemical performance of SiO2-coated LiFePO4 cathode materials for lithium ion battery

Effect of CeO2-coating on the electrochemical performances of LiFePO4/C cathode material

Improve the Structure and Electrochemical Performance of LiNi0.6Co0.2Mn0.2O2 Cathode Material by Nano-Al2o3 Ultrasonic Coating

Structural characterization and electrochemical performance of AlF3-coated LiNi0.45Mn0.45Co0.10O2 as cathode materials for lithium ion batteries

Enhance electrochemical performance of LiFePO4 cathode material by Al-doped Li7La3Zr2O12 and carbon co-coating surface modification

Interfacial effect of nano Al2O3 modifying LiFePO4 to improve capacity retention and rate capability of lithium ion batteries

Improving the Cycling Stability and Rate Capability of LiMn0.5Fe0.5PO4/C Nanorod As Cathode Materials by LiAlO2 Modification

Improvement of Electrochemical Performance for AlF 3 -Coated Li 1.3 Mn 4/6 Ni 1/6 Co 1/6 O 2.40 Cathode Materials for Li-ion Batteries

Synthesis and Electrochemical Performance of Al2O3 Coated LiNi0.03Co0.05Mn1.92O4 as Cathode Material

Effect on Electrochemical Property of LiNi1/3Co1/3Mn1/3O2 by AlPO4 Nano-Coating

Enhanced Electrochemical Property of FePO4-coated LiNi0.5Mn1.5O4 As Cathode Materials for Li-ion Battery

Improving the Ni-rich LiNi0.5Co0.2Mn0.3O2 cathode properties at high operating voltage by double coating layer of Al2O3 and AlPO4

Improving the Electrochemical Performance of Ni-rich Cathode Material LiNi 0.815 Co 0.15 Al 0.035 O 2 by Removing the Lithium Residues and Forming Li 3 PO 4 Coating Layer

LiNi0.8Co0.15Al0.05O2 Cathodes Exhibiting Improved Capacity Retention and Thermal Stability Due to a Lithium Iron Phosphate Coating