Abstract:Experiments have been carried out to study the relationship between the addition of tantalum and microstructure, especially the formation of the B2 phase in lamellar colonies. The mechanical properties, with different contents of Ta, were also measured. Ti46Al8Nb2.6CxTa alloys were prepared by casting with the content of Ta varying from zero to 1.0 at.%. Experimental results show that the B2 phase forms in lamellar colonies with the addition of Ta, and its content increases when the content of Ta increases. Meanwhile, the γ phase decreases and the lattice parameter of the α 2 phase increases. The size of the lamellar colony decreased from 29.9 to 21.6 μm. Ta dissolves into Ti2AlC by substitution, and its solubility is more than 1.1% tested by EDS. Nb, which is necessary for the formation of the B2 phase, comes from two aspects. The first is that Ta dissolves into the Ti2AlC and partly replaces the Nb atom and the second is the decrease in the γ phase because it has higher solid solubility for Nb. The increase in Nb in the liquid phase increases the composition supercooling and heteronucleation at the solidification front, which accounts for refining the lamellar colony. Room temperature compressive testing showed that the compressive strength and the strain increased when the Ta content increased up to 0.8% and then decreased. Improvement of the compressive properties resulted from the grain boundary strengthening and their decrease induced by more content of the B2 phase. Tensile properties, at elevated temperature, were improved with testing temperature increasing from 750 to 950°C, because solid solution strengthening is a major influence factor.

Microstructure Evolution and Mechanical Properties of LaB6-modified Ti2AlNb Alloy Fabricated by Blended Elemental Powder Metallurgy

Effect of LaB6 on the Microstructure Evolution and Mechanical Properties of Ti-45Al-8Nb Alloy

Investigation on the Microstructure and Mechanical Behaviors of a Laser Formed Nb-Ti-Al Alloy

Effect of Trace Boron Addition on the Microstructural Evolution and Mechanical Properties in Ti45al8nb2cr-B Alloys

Microstructure, Mechanical, and Tribological Properties of Nb-Doped TiAl Alloys Fabricated via Laser Metal Deposition

Mechanical Properties and Oxidation Characteristics of TiNiAl(Nb) Intermetallics

Effect of La on Microstructure, Mechanical Properties and Friction Behavior of In Situ Synthesized TiB2/6061 Composites

Effects of Tantalum on Microstructure Evolution and Mechanical Properties of High-Nb TiAl Alloys Reinforced by Ti2AlC

Effects of La on microstructure and mechanical properties of NbMoTiVSi0.2 refractory high entropy alloys

Grain refinement of additive manufactured Ti-6.5Al-3.5Mo-1.5Zr-0.3Si titanium alloy by the addition of La2O3

Investigation on the Microstructure and Mechanical Properties of the Ti-Ta Alloy with Unmelted Ta Particles by Laser Powder Bed Fusion

Microstructure and Mechanical Property Improvement of Laser Additive Manufacturing Ti–6Al–4V via the Niobium Addition

Effects on Mechanical Properties of Refractory Metal Doped Ti3al Alloy

Effect Of La, Zr Micro-Alloying On The Microstructure And Mechanical Properties Of Al-5mg-0.2ti Alloy

Promoting the heterogeneous nucleation and the functional properties of directed energy deposited NiTi alloy by addition of La2O3

Optimization of Processing Parameters and Microstructure Evolution of (TiB+La 2 O 3 )/Ti6Al4V Manufactured by Laser Melting Deposition

Microstructure evolution and enhanced mechanical properties in Al-Mn alloy reinforced by B-doped TiC particles

Effect of Nb and B on the Precipitation Behaviors in Al-Ti-Nb Balanced Ratio Ni-Based Superalloy: A Phase-Field Study

Effect of LaB6 addition on the in-situ synthesis of TiB /Ti Ni /TiC reinforced Ni-based composite coatings

Enhanced Hot Workability of Ti–46Al–4Nb–0.1B Alloy by Introducing Adjustable β Phase via Elemental Powder Metallurgy

Uncovering the roles of LaB6-nanoparticle inoculant in the AlSi10Mg alloy fabricated via selective laser melting