Abstract:Effect of injection temperature and speed on the bonding strength of PA‐Al composite structure. Lightweight and high‐strength polymer–metal hybrid structures are favored for reducing material and energy consumption. In this study, carbon fiber‐reinforced polyamide 6 (CFPA) composite materials were prepared through melt blending, and 30 wt% CFPA exhibited the highest shear strength and lowest shrinkage rate among other carbon fiber contents. With pretreatments of anodizing and etching treatment, injection molded direct joining was employed to create polyamide 6 (PA)/CFPA–Aluminum alloy (Al) composites. The impacts of the injection temperature and speed on the bonding strength of the PA/CFPA–Al composite materials were investigated. The characterization results confirmed that carbon fiber doping reduces the coefficient of linear thermal expansion (CLTE) and enhances crystallization ability of PA. The higher injection temperatures and lower injection speed significantly increase the crystallinity of PA and the infiltration of the molten polymer into the nanoporous anodic aluminum oxide films. When the injection temperature was 270°C and the speed was 6 mm/s, the bonding strength of the PA–Al hybrid structure reached a maximum of 36.6 MPa. When the injection temperature was 300°C, the bonding strength of the CFPA–Al hybrid structure reached a maximum of 40.8 MPa. Adhesive parts with high shear bonding strength are critical to satisfying engineering requirements and have significant potential, particularly in polymer–metal composite structures. The polymer‐metal hybrid structure can meet the high interfacial bonding strength required in most engineering applications. Highlights Injection temperature and speed in IMDJ affect PA crystallinity. Carbon fiber doping reduces the CLTE of PA and increases the shear strength. High temperatures and low injection speeds are beneficial to adhesives. The bonding strength of PA–Al reached a maximum of 36.6 MPa. The bonding strength of CFPA–Al reached a maximum of 40.8 MPa.

Enhanced Thermal Properties of Polyamide 6, 6 Composite/aluminum Hybrid Via Injection Joining Strategy

Improved Thermal Conductivity of Ceramic Filler‐filled Polyamide Composites by Using PA6/PA66 1:1 Blend As Matrix

Enhanced Thermal Conductivity in Polyamide 6 Composites Based on the Compatibilization Effect of Polyether-Grafted Graphene

Ultra‐high bonding strength of carbon fiber–doped polyamide–aluminum alloy composite structure achieved by changing crystallinity

Enhanced Thermal Conductivity of Polypropylene/polyamide 6 Composites Via Optimizing the Selective Distribution of H-Bn and NH2-CNTs Hybrid Fillers Within the Co-Continuous Structure

Thermal Deformation of PA66/Carbon Powder Composite Made with Fused Deposition Modeling

Hybrid of multi‐dimensional fillers for thermally enhanced polyamide 12 composites fabricated by selective laser sintering

A double mixing process to greatly enhance thermal conductivity of graphene filled polyamide 6 composites

Additive Manufacturing of Polyamide 66: Effect of Process Parameters on Crystallinity and Mechanical Properties

Improved out-of-plane thermal conductivity of boron nitride nanosheets filled polyamide 6/polyethylene terephthalate composites by rapid solidification method

Enhancing flame retardancy and heat insulation performances of polyamide 66 composite film by adding CNC/Al2O3 nanohybrids

Development of polyamide 6‐graphene oxide nanocomposite and direct‐joining with aluminum alloy for lightweight engineering applications

High-performance thermal insulating polyamide 6/66–cesium tungsten bronze composite hollow fiber via melt spinning and melt mixing

Concurrent enhancement of dimensional stability and thermal conductivity of thermoplastic polyamide 12T/Boron nitride composites by constructing oriented structure

Novel AA7075/AA2124-SiC-17p laminated structures for aerospace applications: A Comparative study into the mechanical performance of PA6 and PA66 composite interlayers

Micro-nano interfacial mechanical interlocking structure-property of the ultrasonic-assisted hot press molded polypropylene/aluminum alloy hybrid

Polymer Composite with Enhanced Thermal Conductivity and Insulation Properties through Aligned Al2O3 Fiber

Thermal conductive nylon 6 composites using hybrid fillers to construct a three‐dimensional thermal conductive network

Low-temperature Nanowelding between Graphene and Carbon Nanotubes for High Performance of Polyamide 66 Composites

Enhanced Mechanical Property of Polyamide-6/Graphite Sheet Composites with Segregated 3D Network Binary Structure for High Thermal Conductivity

Thermal Conductive Nylon 6 Composites with Hybrid Fillers Prepared Through Reaction During Extrusion