Abstract:Fatigue damage is generally described as the nucleation and growth of cracks to final failure. These two stages of fatigue damage are often modeled with completely different methods with no quantitative relationships between them. In addition, a number of fitting parameters are needed in order to consider different effects. The current work is aimed to develop a robust approach for the prediction of fatigue life from crack initiation to final fracture. The approach bridges the gap between the crack nucleation and growth regions. Based upon the conception that fatigue damage is directly related to the stresses and strains inside the material, it is assumed that both crack nucleation and crack growth are governed by the same fatigue damage mechanisms and a single fatigue damage criterion can model both stages. A basic rule is that any material point fails to form a fresh crack if the total accumulated fatigue damage reaches a limit. Crack growth is treated as a process of continuous crack nucleation without using the stress intensity factor or J-integral concept. The approach consists of two steps: stress analysis and fatigue damage prediction. Elastic-plastic stress analysis is conducted for the component to obtain the detailed stress-strain responses. By using a general fatigue criterion, fatigue crack nucleation and growth are predicted. Notched specimens made of 1070 steel were experimentally tested from crack initiation till fracture. The approach was applied to predict the fatigue life of 1070 steel and the predicted fatigue lives were in excellent agreement with the experimental observations.

A Novel Damage Model of Fatigue Life Prediction for Metallic Structures

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

Multiaxial Fatigue Life Prediction Based on Damage Mechanics and Critical Plane Method

Life Prediction of Corrosion-Fatigue Based on a New Crack Growth Rate Model with Damage and the Extended Finite Element Method

A Continuum Damage Mechanics Approach for Fatigue Life Prediction of Open-Hole Metallic Plate

A New Model For Predicting Crack Initiation Life In Thin Walled Tubes Under Multiaxial Proportional Loading

Fatigue life prediction model of metallic materials considering crack propagation and closure effect

A Nonlinear Fatigue Damage Model for Life Prediction of Composite Laminates

A Fatigue Crack Quantification Model for Metallic Structure Based on Strain Monitoring Data

A Novel Fatigue Life Model Considering Surface-Damage Induced Performance Degradation

A Life Prediction Model for Low Cycle Fatigue Based on Continuum Damage Mechanics

An Approach for Fatigue Life Prediction

A Modified Nonlinear Damage Accumulation Model for Fatigue Life Prediction Considering Load Interaction Effects

An Improved Prediction Model on Fatigue Crack Growth Rate under Variable Amplitude Loads for Metallic Materials

Bi-variable Damage Model for Fatigue Life Prediction of Metal Components

A New Damage Mechanics Based Approach to Fatigue Life Prediction and Its Engineering Application

Structural mechanics model for anisotropic damage and fatigue life prediction method of face-centered cubic metal materials

A continuum damage model for prediction of crack initiation life of pitting corrosion and fatigue

A Novel Approach for Corrosion Fatigue Life Estimation under Asymmetric Cyclic Loadings Using Intrinsic Damage Dissipation

A Multi-Scale Damage Model for Fatigue Accumulation Due to Short Cracks Nucleation and Growth

Continuum Damage Mechanics Combined with the Extended Finite Element Method for the Total Life Prediction of a Metallic Component