Abstract:In the present paper, the effects of thermal insulation cover curing on the rise in temperature of concrete, and further on the mechanical properties of the concrete are measured experimentally. In the experiments, polyurethane foam boards of 100 mm thickness were used for thermal insulation, and three concrete strength grades of C30, C50 and C80, were used as concrete samples. Conventional standard curing, and two heat curing methods with a constant temperature of 40 °C and 60 °C were used for comparison. The pore structure of the cement paste subject to the different curing procedures, including insulation cover curing, heat curing and standard curing, was experimentally measured using mercury intrusion porosimetry. The test results show that rate of increase in compressive strength compared with standard curing is 22–34%, 16–26%, and 23–67%, respectively, for C30, C50, C80 concrete after being subject to 1 to 3 days thermal insulation cover curing in the initial period after concrete casting. As expected, initial heat curing of concrete will result in a reduction in the long-term strength of the concrete. At 28 days, the strength reduction rate compared with standard curing due to the insulation cover curing is 3.1–5.9%, 0.6–3.0%, 0–3.2%, respectively, for C30, C50, C80 concrete. By contrast, the compressive strength reduction compared with standard curing at 28 days is 8.6–10.5%, 8.6–9.1%, 4.7–5.6%, respectively, for C30, C50, C80 concrete after being subject to a constant heat curing of 40 °C and 60 °C in the initial period after concrete casting. Measurement of the pore structure of the paste subject to different curing procedures initially after casting shows that rising curing temperature leads to coarser pores, especially an increase in capillary pore fraction. Among the four curing methods used in the present study, the effect of insulation cover curing and low temperature (40 °C) heat curing on the capillary pore content is small, while the effect of high temperature (60 °C) heat curing is significant.

Determination of the apparent activation of concrete by adiabatic test and simulation of self-heated curing process at early age

Performance of concrete containing fly ash at early ages

Apparent Activation Energy of Concrete in Early Age Determined by Adiabatic Test

Evaluation of Early Age Mechanical Properties of Concrete in Real Structure

Effect of Curing Conditions on Property of High Performance Concrete with Composite Mineral Admixture

Cement Hydration Based Model to Predict the Mechanical Properties of Precast Concrete

Study on Shear Behavior of Concrete-polymer Cement Mortar at Elevated Temperature

The Influence of High-Temperature Curing on the Hydration Characteristics of a Cement–ggbs Binder

Influence Mechanism of Initial Concreting Temperature and Water-Binder Ratio on Hydration Rate of Fly Ash Concrete

Experimental study of macroscopic and microscopic properties of long-age hydraulic concrete based on high-temperature accelerated curing

Evaluate the effect of coarse aggregates on cement hydration heat and concrete temperature modelling using isothermal calorimetry

Influence of Steam Curing Method on the Performance of Concrete Containing a Large Portion of Mineral Admixtures

Influence of Early-Age Moist Curing Time on the Late-Age Properties of Concretes with Different Binders

Effects of Curing Regimes on Strength Development of High-Strength Concrete

Effect of Curing Temperature on Strength Development of Cement-Asphalt Mortars

Experimental Study of Thermal-Hydraulic-Mechanical Coupling Behavior of High-Performance Concrete

Experiment and Analysis of Concrete Adiabatic Temperature Rise

The Influential Factors of Adiabatic Temperature Rise of Concrete

Cement Hydration Rate of Ordinarily and Internally Cured Concretes

Effect of the Thermal Insulation Cover Curing on Temperature Rise and Early-Age Strength of Concrete

High-temperature performance of ambient-cured alkali-activated binder concrete