Abstract:Magnetoresistance having a field and current dependence like that of GMR (but a rather small magnitude) has been observed in Co70Fe30/GeTe and Co70Fe30/Ge2Sb2Te5 granular films. Film stacks were fabricated using tandem (multilayer) deposition and annealing was required for the films to develop the GMR-type response. This GMR-type behavior is distinct from AMR, which is observed before annealing. With films having the structure [CoFe 4 nm/GeTe 6 nm]10, a magnetoresistance (MR) of 0.19 %, which has the GMR-type character can be observed after an optimal annealing temperature of 450 °C. TEM and X-ray reflectometry suggest that columnar granules with layered Fe form during deposition and with annealing. Magnetoresistive transport is believed to be between the discontinuous layers in each columnar grain. These discontinuous layers are observed to be superparamagnetic in SQUID ZFC-FC measurements measured from 5–300 K. Magnetoresistance can be fitted by the quadratic relation appropriate for GMR in granular films, especially at higher GeTe compositions. When Ge2Sb2Te5 is used instead of GeTe, higher anneal temperatures are required before the MR with GMR character appears. This GMR type response does not appear when pure Fe is used instead of the CoFe alloy, with the samples showing only AMR in this case. This is due to the absence of Co which seems to cause a more granular growth.

Study on Magneto-Refractive Effects in (cofe)1－xagx Granular Thin Films

Study on GMR in CoAg Thin Granular Films

Preparation and Microstructures of CoAg Granular Films with Giant Magnetoresistance

Giant Magnetoresistance Effect and Microstructure of Fe-Cu Granular Films

Giant Magnetoresistance and Microstructures in CoAg Granular Films Fabricated Using Ion-Beam Co-Sputtering Technique

Preparation and GMR of (FeCo)-Ag Granular Films

Giant Magnetoresistance and Microstructure of Co-Cu and Feco-Cu Granular Films

Domain Observation and Transition from Giant Magnetoresistance to Anisotropy Magnetoresistance in Ag1−x(Ni0.8Co0.2)x Granular Films

An Optical Method of Contactless Measurement of Giant Magnetoresistance Effects in Magnetic Multi-Layer Films

Dependence of Giant Magnetoresistance on Microstructures in Ion-Beam Co-Sputtered Coxag1-X Granular Films

A Phenomenological Theory of the Granular Size Effect on the Giant Magnetoresistance of Granular Films

The Influence of Particle Size on Magneto-Optical Kerr Effect in Fe45Ag55 Granular Films

Giant Magnetoresistance Properties in Granular Type (Co-Ag)/ag Multilayers

Magnetoresistance in Granular Films Formed by CoFe and Phase Change Material

Giant Magnetoresistance in Granular Type (Co-Ag)/ag Multilayers

Magneto-optical Kerr Effect in Co X Ag 1- X Nanostructured Granular Films

Magnetism And Magnetoresistance Studies Of Hffe6ge6-Type Y1-Xcexmn6sn6 (X=0.1-0.3) Compounds

FMR Study on Some Magnetic Granular Films

Gmr and Characterization of Microstructures in Ion-Beam Cosputtered Coag Granular Films

Key Role in Giant Magnetoresistance of Granular Films: Single-Domain Ferromagnetic Granules

Giant Maganetoresistance and Microstructure of Fe-Al2O3 Nanogranular Films