Influence of Preparation Parameters on the Frictional Behavior of PVA Hydrogel Against Glass Substrate

Peng-peng Xu,Miao Du,Qiang Zheng

DOI: https://doi.org/10.3724/sp.j.1105.2014.13377

2014-01-01

Abstract:Poly ( vinyl alcohol ) ( PVA ) hydrogels were prepared under different conditions such as the various concentrations, solvents, the times of freeze-thaw circles and the introduction of polyethylene oxide ( PEO ). Effect of these preparation parameters on the frictional behavior of PVA hydrogels sliding on a glass surface was investigated in detail. The results show that mixed solvent of water and dimethyl sulfoxide facilitates the formation of a more uniform gel network and thus increases the strength of hydrogels. Moreover,the strength of hydrogels can also be increased by increasing freeze-thaw circle times and adding ultrahigh molecular weight PEO due to the formation of a dense and uniform network. On the other hand, stiff hydrogels with high modulus show a higher frictional stress at a low sliding velocity compared with soft hydrogels; however, it is fast to get into the hydrodynamic lubrication and exhibits a lower frictional stress at a high sliding velocity. The velocity (10 (-1) similar to 10(0) m/s) is approximately the cartilage sliding velocity of the knee when people are walking. In addition,PEO molecular brush can reduce the frictional stress of PVA sliding against glass at high sliding velocities to some extent, however, at low sliding velocities, the reducing of frictional stress depends on the concentration of the added PEO. It suggests that increasing the modulus of hydrogels is more effective in reducing the friction at high sliding velocity region than that of introducing PEO with ultrahigh molecular weight.