Abstract:A novel DOPO derivative (DIDOPO) is incorporated together with amine-based multi-walled carbon nanotubes (MWCNTs) into PA6 by melt blending. Mechanical properties, thermal stability, crystallinity, and combustion properties are measured using universal testing machine, thermogravimetric analyzer, differential scanning calorimeter, and cone calorimeter, respectively. After combustion, the morphology of char layer is further observed by a scanning electron microscope. The results show that MWCNTs-incorporated flame-retardant nanocomposites exhibit a tensile strength that is 55% higher than that of the PA6/DIDOPO composites. From the TG and DTG curves, it can be seen that the T-5wt% of PA6 composites increased slightly and the maximum weight loss rate temperature (T-max) gradually improved after adding MWCNTs, indicating that the addition of MWCNTs delays the process of thermal degradation of the PA6 composites. With the incorporation of MWCNTs, the amount of residual carbon is also increased. From the non-isothermal crystallization curve, it can be seen that the crystallization initial temperature (T-onset) and crystallization peak temperature (T-c) of the PA6 composites are significantly improved with the addition of MWCNTs. However, the crystallinity is lower due to the heterogeneous nucleation of the MWCNTs. From UL-94 datas, the combustion time (t(1) + t(2)) is increased with the incorporation of MWCNTs into PA6/DIDOPO composites, which results in a V-1 level in the UL-94 test and a slightly increased LOI value. This phenomenon can be attributed to an increment in melt viscosity and a decrement in flow properties. Combined with the curves of effective combustion heat, total smoke release and CO release rate, it can be concluded that the synergistic effect between MWCNTs and DIDOPO weakens the thermal degradation process of the PA6 composites, thus increasing the incomplete combustion and reducing the complete combustion of the PA6 composites, which is beneficial to the flame retardance of the materials. Addition of 2 wt% MWCNTs results in a peak heat release rate (PHRR) of 367.28 kW/m(2), which corresponds to a 58.9% lower rate than that of pure PA6, as revealed by cone calorimetry. Based on SEM and Raman, a continuous and compact char layer is observed upon addition of MWCNTs, which is ascribed to a synergistic effect between MWCNTs and DIDOPO.

Synergistic Flame Retardancy of Amine-based Multi-walled Carbon Nanotubes/DOPO Derivatives and Its Effect on the Properties of Nylon 6

Enhancing flame retardant and antistatic properties of polyamide 6 by a grafted multiwall carbon nanotubes

Nanoclay, intumescent flame retardants, and their combination with chemical modification for the improvement of the flame retardant properties of polymer nanocomposites

Enhancing the flame retardancy and UV resistance of polyamide 6 by introducing ternary supramolecular aggregates

Preparation and Combustion Properties of Flame Retardant Nylon 6/Montmorillonite Nanocomposite

A Phosphorus-Nitrogen Containing Dendrimer Reduces The Flammability Of Nanostructured Polymers With Embedded Self-Assembled Gel Networks

Preparation and Characterization of DOPO-Functionalized MWCNT and Its High Flame-Retardant Performance in Epoxy Nanocomposites

The Synthesis of Meltable and Highly Thermostable Triazine‐dopo Flame Retardant and Its Application in PA66

Functionalized Carbon Nanotubes with Phosphorus- and Nitrogen-Containing Agents: Effective Reinforcer for Thermal, Mechanical, and Flame-Retardant Properties of Polystyrene Nanocomposites

The effect of carbon nanotubes/NiFe2O4 on the thermal stability, combustion behavior and mechanical properties of unsaturated polyester resin

Effect of multiple reactions induced by a flame retardant containing P/N/S and chain extender on fire safety and mechanical performance of polyamide 6

Multi-walled Carbon Nanotubes Encapsulated by Graphitic Carbon Nitride with Simultaneously Co-Doping of B and P and Ammonium Polyphosphate to Improve Flame Retardancy of Unsaturated Polyester Resins

P, N-decorated halloysite nanotubes for flame retardancy enhancement of polyamide 6/aluminum diethylphosphinate

The flame retardancy and rheological properties of PA6/MCA modified by DOPO-based chain extender

Improving flame retardancy and mechanical properties of polyamide 6 induced by multiple reactions among flame retardants and matrix

Effect of different IFS (MWCNTs, BN, and ZnO) on flame retardant, thermal and mechanical properties of PA6/aluminum diisobutyl phosphinate composites

Cooperative Effect of ZIF-67-Derived Hollow NiCo-LDH and MoS2 on Enhancing the Flame Retardancy of Thermoplastic Polyurethane

Functionalized MWCNTs modified flame retardant PLA nanocomposites and cold rolling process for improving mechanical properties

[Inflammation biomarkers capacity in predicting the metabolic syndrome].

Effect of combustion residue structure on flame retardancy of HIPS/multiwall carbon nanotube composites

Synergistic flame‐retardancy of lamellar cerium phenylphosphonate and aluminum diethylphosphinate towards suppressing "candlewick effect" of polyamide 6/carbon fiber composites