Functionalized Zr‐MOFs for Enhancing Flame Retardancy and Smoke Suppression Performance on TPU
Qi Yao,Shaoquan Li,Jianfeng Ban,Bo Yang,Tiwen Xu,Hegang Ren,Yuxin Huang
DOI: https://doi.org/10.1002/slct.202401227
2024-06-20
ChemistrySelect
Abstract:In the process of thermal decomposition, Zr‐MOFs can generate metal oxides and some non‐flammable gases. The metal oxides can form a physical barrier to protect the associated polymers from further combustion and effectively adsorb gases and fumes. The releasing non‐flammable gases can dilute the concentration of flammable gases. These processes will reduce the amount of available fuel burned, thereby reducing heat release and smoke formation. Metal‐Organic Framework (MOF) materials can be used as flame‐retardants and smoke suppressants for polymers. As a MOF material, UIO‐66(Zr) possesses higher thermal stability and controllable pore size. In this paper, UIO‐66(Zr), NH2‐UIO‐66(Zr), and SiO2, MWCNT, and GO functionalized NH2‐UIO‐66(Zr) was fabricated to improve the flame retardant and smoke suppression performance of thermoplastic polyurethanes (TPU). The experimental results show that compared with neat TPU (LOI value 19.1 %), 2 % usage of UIO‐66(Zr) and NH2‐UIO‐66(Zr) can endow TPU with 26 % LOI value and vertical combustion rating of V‐1. Moreover, SiO2, MWCNT, and GO functionalized NH2‐UIO‐66(Zr) provide TPU with above 27.8 % LOI value and vertical combustion rating of V‐0. Meanwhile, the CCT results showed that the peak heat release rate and total heat release of TPU‐U5 (added 2 % GO‐modified NH2‐UIO‐66(Zr)) are 299.52 Kw ⋅ m−2 and 68.21 MJ m−2, much lower than that of neat TPU, which are 1180.05 Kw ⋅ m−2and 104.87 MJ m−2, respectively. The TGA, char residue EDS and XRD analysis show that SiO2, MWCNT, and GO functionalized NH2‐UIO‐66(Zr) could generate zirconium metal oxide during the combustion process, which acts as a physical barrier to prevent the TPU matrix by promoting the generation of carbonization layer. The zirconium metal oxide and carbonization layer also can confine flammable gases, which can delay the ignition time and hinder the overflow of gas. In addition, NH2‐UIO‐66(Zr) could generate non‐flammable N2 diluting the concentration of flammable gases. The mechanical properties of TPU composites can maintain more than 87 % of the neat TPU after the addition of 2 % SiO2, MWCNT, and GO functionalized NH2‐UIO‐66(Zr). These results indicate that functionalized Zr‐MOFs composites could act as excellent flame‐retardants in TPU.
chemistry, multidisciplinary