Abstract:Fluorenyl polyphosphazene (PZFP) microspheres were facilely prepared through a one-step precipitation copolymerization of hexachlorocyclotriphosphazene (HCCP) and 4,4' -(9-fluorenylidene) diphenol under ultrasonic. PZFP microspheres were incorporated into polybenzoxazine resins to improve the flame properties of the polymers. The results of thermogravimetric analysis (TGA), cone calorimeter (CONE) and dynamic thermal mechanical analysis (DMA) showed that incorporation of PZFP microspheres enhanced the char residues amount of PBa during thermal degradation process, reduced the heat release rate (HRR), delayed the time to ignition (TTI) and increased the fire performance index (FPI) of PBa in fire. Interestingly, PBa/PZFP-10% showed the relatively best flame retardant properties among a series of PBa/PZFP composites with different PZFP contents. In comparison to pure PBa, the HRR value in the composite PBa/PZFP-10% was reduced to 214 kW.m(-2) from 566 kW.m(-2) for pure PBa, and FPI value was enhanced to 0.243 from 0.087. The glass transition temperature (T-g) and storage modules of PBa/PZFP-10% were increased slightly, with the introduction of 10% PZFP microspheres. The Tg of PBa and PBa/PZFP-10% was 222 and 226 degrees C, respectively. It is believed that PZFP microspheres offered PBa resins good flame retardant properties, without affecting the application temperature of PBa. The char residue analysis using scanning electron microscopy (SEM) suggested the formation of high-quality char layer with compact outer surfaces and polyphorous inner structure. The volatile products formed in the thermal degradation process of PBa and PBa/PZFP composites were detected by a TGA-Fourier transform infrared spectrometer (TGA-FTIR). The improved flame retardancy of PBa/PZFP composites was mainly attributed to a combination of the greatly increased melt viscosity of PBa and matrix fast swelling due to the pyrolytic gases. Additionally, PZFP microspheres was found to greatly reduce the amount of pyrolytic gases containing N-H and -C = C = C- groups. Instead, it released phosphorous-containing species to achieve flame retardancy in the gas phase. PZFP microspheres contributed a synergistic condensed phase and gas phase flame retardant mechanism for PBa resins.

Effects of Fluorenyl Polyphosphazene Microspheres on the Flame Retardant Properties of Polybenzoxazine Resins

Improving the flame retardancy and mechanical properties of high-density polyethylene-g-maleic anhydride with a novel organic metal phosphonate

Polybenzoxazine Resins with Cellulose Phosphide: Preparation, Flame Retardancy and Mechanisms

Flame-retardant effect of hyperbranched phosphazene-based microspheres in poly(L-lactic acid)

Nanoclay, intumescent flame retardants, and their combination with chemical modification for the improvement of the flame retardant properties of polymer nanocomposites

Preparation and Properties of Toughened/flame‐retardant PA6/glass‐fiber Composites Reinforced by Linear Polyphosphazene Elastomers

A Phosphorous-Containing Bio-Based Furfurylamine Type Benzoxazine and Its Application in Bisphenol-A Type Benzoxazine Resins: Preparation, Thermal Properties and Flammability

Synthesis of Organic-Inorganic Hybrid Aluminum Hypophosphite Microspheres Flame Retardant and Its Flame Retardant Research on Thermoplastic Polyurethane

Study on novel boron-containing triazine flame retarded thermoplastic polyester elastomer composites and the flame retardant mechanism

Effect of prepared barium phytate on thermal stability and combustion properties of flexible polyurethane foams

Effect of weak intermolecular interactions in micro/nanoscale polyphosphazenes and polyethylene terephthalate composites on flame retardancy

Investigation of a Combination of Novel Polyphosphoramide and Boron-Containing Compounds on the Thermal and Flame-Retardant Properties of Polystyrene

Effects of Fluorinated Side Groups on the Insulation Performances of Polyphosphazenes with Organic Fiber Reinforcement

Flammability and Carbonization of High-Impact Polystyrene/α-Zirconium Phosphate Nanocomposites

Phosphorus/Bromine Synergism Improved the Flame Retardancy of Polyethylene Terephthalate Foams

Effect of zinc borate on the fire and thermal degradation behaviors of a poly(3-hydroxybutyrate-co-4-hydroxybutyrate)-containing intumescent flame retardant

Synergistic effect of zinc borate and microencapsulated black phosphorus nanosheets for improved flame retardancy and smoke-suppression performance of epoxy resin

Morphologies and thermal properties of flame-retardant polystyrene/α-zirconium phosphate nanocomposites

Preparation and characterization of polyphosphazene-based flame retardants with different functional groups

To improve the flame retardancy, mechanical properties and degradation rate of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) by divinybenzene-maleic anhydride microsphere

A Novel Branched Phosphorus-Containing Flame Retardant: Synthesis and Its Application into Poly(Butylene Terephthalate)