Preparation and characterization of organopalygorskites and their application for p nitrophenol adsorption

Binoy Sarkar,Yunfei Xi,Mallavarapu Megharaj,G Krishnamurti,Ravi Naidu

2010-01-01

Abstract:Telephone:+ 618 83026293, Fax:+ 618 83023057 Organoclays are prepared by modifying clays with alkyl ammonium cations. The organoclays thus produced have wide range of environmental application for the adsorption and removal of toxic environmental contaminants in soil and water. The 2: 1 swelling type clays are mostly used for organoclay preparation. However, the organoclays prepared from swelling type clays have limited applicability for environmental remediation under flow conditions. Being a non-swelling clay and having high surface area, palygorskite is a good candidate to be modified organically for environmental application under flow conditions. However, unlike 2: 1 swelling type clays, palygorskite is under explored for its potential to prepare organoclays.We prepared two organopalygorskites in cation exchange reaction (Xi et al., 2004) by modifying locally available palygorskite with dimethyldioctadecylammonium bromide (DMDOA) at organic loadings equivalent to 100% and 200% cation exchange capacity (CEC) of the palygorskite. The CEC and BET surface area of the palygorskite were 17 cmol (p+) kg-1 and 97 m2 g-1, respectively. The modification caused reduction in the surface area of the organopalygorskites due to pore blocking that inhibited passage of N2 in the organopalygorskite structures during BET analysis. The 200% CEC equivalent organopalygorskite showed 24 m2 g-1 BET surface area as against 33 m2 g-1 by the 100% CEC equivalent organopalygorskite. The long chained DMDOA cation packed tightly on the palygorskite surface forming a well structured organic phase, which was further supported …