Abstract:Direct ink writing (DIW) of aerogels has great potential in designing novel three-dimensional (3D) multifunctional materials with hierarchical structures ranging from the nanoscale to the macroscopic scale. In this paper, pure aerogels composed of inorganics, strongly cross-linking organics, and weakly cross-linking organics were directly written via the precise control of the gelation degree without using any additives. The rheological properties of a resorcinol–formaldehyde aerogel-based sol–gel ink (marked as RA ink) were measured at different reaction times to determine the suitable printable range (G′LVR: several 103 Pa) that ensures its good print fidelity. In addition, the rheological evolution of the RA ink during the sol–gel process and under different shear stresses was studied. The correlation of relevant parameters was established according to the Hagen–Poiseuille model. Other typical aerogel-based sol–gel inks including a silica aerogel-based sol–gel ink (SA ink) and a polyimide aerogel-based sol–gel ink (PA ink) for DIW were also demonstrated. Finally, water evaporation experiments were carried out using a 3D-printed carbonized resorcinol–formaldehyde aerogel (CA) to further exhibit the potential applications of this novel technology in solar steam generation. The evaporation rate (1.57 kg m–2 h–1) and efficiency (88.38%) of 3D-printed CA were higher than those of bulk CA (1.21 kg m–2 h–1 and 69.82%). This paper systematically studies the control of DIW parameters for aerogel-based sol–gel inks and shows a potential application in high-efficiency 3D-printed evaporators.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c03312?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c03312</a>.Rheological behaviors and thixotropic behaviors of RA inks (Figure S1); rheological behaviors of the SA ink and the PA ink (Figure S2); rapid solidification of the PA ink once it met water (Figure S3); Herschel–Buckley model for RA inks (Figure S4); study of relevant parameters in DIW (Figure S5); extrusion experiments for dextrin (Figure S6); extrusion experiments for RA inks (Figure S7); 3D-printed hydrogels using the RA ink, SA ink, and PA ink (Figure S8); TG-DSC tests for 3D-printed aerogels (Figure S9); uniaxial compression–decompression test for 3D-printed aerogels (Figure S10); derivation of the correlation of the relevant parameters; filament widths at varied applied pressures and writing speeds (Table S1); filament widths at varied heights of the needle to the substrate (Table S2); pressure value, maximum shear stresses, and yield stresses for dextrin and RA inks (Table S3); detailed parameters of bulk CA and 3D-printed CAs (Table S4); and water evaporation data of 3D-printed CAs, bulk CA, and pure water (Table S5).This article has not yet been cited by other publications.

Fabrication of 3D Structures Via Direct Ink Writing of Kaolin/graphene Oxide Composite Suspensions at Ambient Temperature

Direct 3 D Printing of Ultralight Graphene Oxide Aerogel

Direct ink writing 3D printing of graphene/Al2O3 composite ceramics with gradient mechanics

Preparation and Mechanical Performance of SiCw/geopolymer Composites Through Direct Ink Writing

Direct-ink-writing (DIW) 3D printing functional composite materials based on supra-molecular interaction

Direct Ink Writing of Special-Shaped Structures Based on Tio2 Inks

Direct 3D printing of graphene using capillary suspensions

3D printing strong and conductive geo-polymer nanocomposite structures modified by graphene oxide

Direct ink writing of geopolymer with high spatial resolution and tunable mechanical properties

Direct Ink Writing of Mineral Materials: A review

Rheology and Printability of a Porcelain Clay Paste for DIW 3D Printing of Ceramics with Complex Geometric Structures

Printability study of self-supporting graphene oxide-laponite nanocomposites for 3D printing applications

Direct 3D printing of a graphene oxide hydrogel for fabrication of a high areal specific capacitance microsupercapacitor

3D Printing Graphene Oxide Soft Robotics

Study on filament deflection in lattice porous structures fabricated through direct ink writing

Liquid Crystalline 3D Printing for Superstrong Graphene Microlattices with High Density

Three-dimensional printing of complex graphite structures

Unstructured Direct Ink Write 3D Printing of Functional Structures with Ambient Temperature Curing Dual‐Network Thermoset Ink

3D Printing of Graphene Oxide Composites with Well Controlled Alignment

Direct Ink Write (DIW) 3D Printed Cellulose Nanocrystal Aerogel Structures

Versatile Direct Writing of Aerogel-Based Sol–Gel Inks