Microwave Dielectric Properties of High-Entropy [(Mg1/2zn1/2)0.4+x(ni1/3co1/3mn1/3)0.6-X]2tio4 Ceramics
Pingwen Xiang,Yuanming Lai,Linqiao Zhang,Feng Liu,Yuanxun Li,Jiao Han,Yiming Zeng,Qian Liu,Chongsheng Wu
DOI: https://doi.org/10.1016/j.jallcom.2024.177833
IF: 6.2
2024-01-01
Journal of Alloys and Compounds
Abstract:In this study, a series of high-entropy [(Mg1/2Zn1/2)0.4+x(Ni1/3Co1/3Mn1/3)0.6-x]2TiO4 (expressed as MZNCMT) (0.0 ≤ x ≤ 0.6) ceramics were prepared via the solid-state reaction, the high-entropy ceramics exhibited inverse spinel structure. The phase compositions, microstructures, and microwave dielectric properties were investigated. The results of x-ray diffraction (XRD) showed that a principal phase of [(Mg1/2Zn1/2)0.4+x(Ni1/3Co1/3Mn1/3)0.6-x]2TiO4 ceramics, whereas the second phase of (Mg, Zn, Ni, Co, Mn)TiO3 appeared when x ≤ 0.4. With the increase of x value, the relative density of the sample decreased, the unit cell volume first decreased and then kept expanding. This phenomenon could be attributed to the reduction of (Ni1/3Co1/3Mn1/3)2+. Good microwave dielectric properties were achieved: x = 0.0 (εr = 17.17, Qf = 16500GHz, τf = -33 ppm/℃), x = 0.5 (εr = 16.30, Qf = 53900GHz, τf = -30 ppm/℃) and x = 0.6 (εr = 16.26, Qf =110800GHz, τf = -39 ppm/℃), well temperature coefficient of resonance frequency (τf) = -30 ppm/℃ for the sample at x = 0.5, and the highest quality factor (Qf) = 110800GHz for the sample at x = 0.6. The εr value of MZNCMT ceramics is consistent with the theoretical dielectric constant (εtheo), indicating that εr is mainly based on ion polarization. The Qf value were highly related to the packing fraction. Furthermore, the τf value depended on the bond strength of A-site.