Ion release mechanisms in composites containing CaP particles and hydrophilic monomers

Rafael Bergamo Trinca,Beatriz Fonseca Vela,Handially dos Santos Vilela,Roberto Ruggiero Braga
DOI: https://doi.org/10.1016/j.dental.2024.05.008
2024-05-23
Dental Materials Journal
Abstract:Highlights • Replacing BisGMA/TEGDMA by PMGDM/PEGDMA increased composite WS/SL. • Increasing polymer hydrophilicity/permeability increased Ca 2+ release. • The increase was significant only at the highest DCPD and PMGDM/PEGDMA fractions. • In the first two weeks, Fickian diffusion was the predominant mechanism for most tested materials. • In the long term, Ca 2+ released occurred mostly due to relaxational diffusion. Objective To investigate the effect of hydrophilic/permeable polymer matrices on water sorption/solubility (WS/SL), Ca 2+ release, mechanical properties and hydrolytic degradation of composites containing dicalcium phosphate dihydrate (DCPD) particles. Methods Six composites were tested, all with 10 vol% of glass particles and either 30 vol% or 40 vol% DCPD. Composites containing 1BisGMA:1TEGDMA in mols (at both inorganic levels) were considered controls. Four materials were formulated where 0.25 or 0.5 of the BisGMA/TEGDMA was replaced by pyromellitic dianhydride glycerol dimethacrylate (PMGDM)/ polyethylene glycol dimethacrylate (PEGDMA). Composites were tested for degree of conversion (FTIR spectroscopy), WS/SL (ISO 4049) and Ca 2+ release (inductively coupled plasma optical emission spectroscopy). Fracture toughness (FT) and biaxial flexural strength/modulus (BFS/FM) were determined after 24 h and 60 days in water. The contributions of diffusional and relaxational mechanisms to Ca 2+ release kinetics were analyzed using the semi-empirical Salim-Peppas model. Data were analysed by ANOVA/Tukey test (alpha: 0.05). Results WS/SL was higher for composites containing PMGDM/PEGDMA compared to the controls (p < 0.001). Only at 40% DCPD the 0.5 PMGDM/PEGDMA composite showed statistically higher Ca 2+ release than the control. Relaxation diffusion was the main release mechanism. Initial FT was not negatively affected by matrix composition. BFS (both DCPD fractions) and FM (30% DCPD) were lower for composites with hydrophilic/permeable networks (p < 0.01). After 60 days in water, composites with PMGDM/PEGDMA presented significant reductions in FT, while all composites had reductions in BFS/FM. Significance Increasing matrix hydrophilicity/permeability significantly increased Ca 2+ release only at a high DCPD fraction.
materials science, biomaterials,dentistry, oral surgery & medicine
What problem does this paper attempt to address?