Catalytic Conversion of Lignin to Liquid Fuels with an Improved H/C eff Value over Bimetallic NiMo-MOF-Derived Catalysts
Changzhou Chen,Peng Liu,Haihong Xia,Jianchun Jiang,Xiaohui Yang,Minghao Zhou
DOI: https://doi.org/10.1021/acssuschemeng.1c05273
2021-10-06
Abstract:Lignin is an abundant source of aromatics with low effective hydrogen-to-carbon ratio (H/Ceff), and the depolymerization of lignin provides significant potential for producing liquid products with an improved H/Ceff value. In this work, the catalytic conversion of lignin monomers, dimer, trimers, and realistic lignin over spherical MOF-derived catalysts was well established, to get liquid fuels with a higher H/Ceff. The optimal ratio of the catalyst exhibited good hydrodeoxygenation activity and stability for the hydrotreatment of lignin model compounds and lignin. The addition of Mo facilitated the decrease of the particle size of a spherical structure, strengthened the electron-transfer capability between metals Mo and Ni, and enhanced the acid strength. All of these factors contributed to higher hydrodeoxygenation activity in the hydrotreatment process. Up to 100% conversion and 90% yields of ethylcyclohexane and cyclohexanol with H/Ceff values of 2.0 and 1.667, respectively, were obtained. The catalyst achieved a decrease of the oxygen element and an increase of H/Ceff and HHV values. The physicochemical characterizations were performed by various means including X-ray diffraction (XRD), scanning electronic microscopy (SEM), transmission electron microscopy (TEM), H2-temperature-programmed reduction (H2-TPR), NH3-temperature-programmed desorption (NH3-TPD), pyridine-infrared spectroscopy (Py-IR), inductively coupled plasma emission spectrometer (ICP), and Raman and X-ray photoelectron spectroscopy (XPS) analyses, which definitely elucidated the formation of a synergistic effect between metals Mo and Ni. Additionally, a control experiment also illustrated the synergistic effect that facilitated the occurrence of the hydrotreatment process under lower temperatures after the addition of metal Mo. Based on the optimal reaction condition (240 °C, 4 h, 2.0 MPa H2), both lignin and its monomers/dimers/trimers could be effectively hydrotreated to afford liquid products with improved H/Ceff value compared to raw lignin.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c05273.Py-IR spectra of different catalysts (Figure S1); mass balance of hydrogenation under the optimal reaction condition (Figure S2); GC-MS results and product distributions of bio-oil from different lignin feedstocks (Figure S3); and recycling experiments of different lignin feedstocks (Table S1) (PDF)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology