Comparative Study on Microstructure, Corrosion Morphology and Friction Wear Properties of LDH/SC Composite Coatings on Mg‐Li alloy
Ju-mei Zhang,Duo-Duo Lian,An-Rong Hou,Zhi-Hu Wang,Meng-Chun Zhang,Jing Wen Wu,Chao-Chao Wang
DOI: https://doi.org/10.1002/adem.202400058
IF: 3.6
2024-05-19
Advanced Engineering Materials
Abstract:Mg alloy is the preferred material for the lightweight development of manufacturing industry. However, its application is limited due to the poor wear resistance and corrosion resistance. In this experiment, Mg‐Al LDH/SC (Layered double hydroxide/Steam coating) composite coatings were prepared on the surface of LA43M Mg‐Li alloy by steam treatment and in‐situ hydrothermal method for different times (12 h, 18 h, 24 h, 30 h and 36 h). The morphology and structure of the coatings were characterized by SEM, EDS, and XRD, and the friction wear test of the coatings was carried out. The corrosion resistance of the coatings was evaluated by immersion tests and hydrogen evolution experiments. The effect of hydrothermal time on the growth characteristics, wear resistance, and corrosion behavior of LDH/SC coatings in 3.5 wt.% NaCl solution was systematically investigated. In addition, the growth mechanism and corrosion resistance mechanism of the LDH/SC coating were discussed. The results show that the composite coatings is mainly composed of LDH and Mg(OH)2 phases. Appropriately prolonging the hydrothermal reaction time is beneficial to the nucleation and growth of LDH. When the hydrothermal time is 30 h, the prepared coating has the best density, and the prepared coating can significantly improve the corrosion resistance and friction wear properties of the substrate. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary