The manufacture, optical properties, and mechanical aspects of europium-doped borate glasses
Gharam A. Alharshan,A. M. A. Mahmoud,Nasra M. Ebrahem,Ragab A. Elsad,Shaaban M. Shaaban,Mohamed Elsafi,Shimaa Ali Said
DOI: https://doi.org/10.1038/s41598-024-66939-5
IF: 4.6
2024-10-04
Scientific Reports
Abstract:An investigation into the optical and mechanical properties of a novel borate glasses with the chemical composition of 70 B 2 O 3 -10 Li 2 O-10ZnO-5Bi 2 O 3 -5CaO-xEu 2 O 3 was conducted. The glassy specimens of Eu 3+ -doped borate were prepared by the melting-quenching technique. An enhanced density from 3.0860 to 3.2176 g cm −3 and reduced molar volume from 29.27819 to 29.17447 (cm 3 mol −1 ) are the outcome of increasing the concentration of Eu 3+ in glasses. Plotting the extinction coefficient, dielectric constant (ε 1 , ε 2 ), and refractive index (n) against wavelength reveals that they all rise as level of Eu 3+ elements in the glass lattice increases. An increase in Eu 3+ concentration results in a decrease in both the volume (VELF) and surface (SELF) energy loss functions. Also, all elastic-mechanical moduli (such as Young's, Bulk, Shear, and Elongation) increase with increasing the quantity of Eu 3+ ions in the glass lattice. The Young's modulus (Y, GPa) of the glassy specimens was 34.512, 36.089, 36.504, 36.730 and 37.114 GPa for x equal 0, 0.25, 0.5, 0.75 and 1 mol ratio in the glass system, and coded by Eu-0.0, Eu-0.25, Eu-0.5, Eu-0.75 and Eu-1.0, respectively. Growing Eu 2 O 3 levels resulted in an increase in Micro-Hardness from 2.050 to 2.146 GPa. Poisson's ratio values for Eu-0.0, Eu-0.250, Eu-0.5, Eu-0.75 and Eu-1.0 were 0.273, 0.275, 0.277, 0.277 and 0.278, respectively.
multidisciplinary sciences