Luminescence properties of Eu 3+ -doped potassium-gadolinium-phosphate glasses
D. Yodkantee,A. Prasatkhetragarn,N. Wantana,N. Chanthima,S. Kothan,N. Intachai,R. Yimnirun,H.J. Kim,J. Kaewkhao
DOI: https://doi.org/10.1016/j.ijleo.2024.171681
IF: 3.1
2024-02-09
Optik
Abstract:Eu 2 O 3 -doped K 2 O-Gd 2 O 3 -P 2 O 5 glasses were fabricated using the melt-quenching technique. The result indicates that the glasses' density and refractive index increase while the molar volume decreases from 0.05 to 0.5 mol% and then increases from 0.5 to 2 mol% with increased Eu 2 O 3 concentration. The absorption spectra in the UV-Vis and NIR regions exhibit an energy transition from a ground state to possible excited states for 7 F 0 → 5 K 5 , 7 F 0 → 3 P 0 , 7 F 1 → 5 G 2 , 7 F 0 → 5 L 6 , 7 F 1 → 5 D 3 , 7 F 0 → 5 D 2 , 7 F 1 → 5 D 1 and 7 F 0 → 7 F 6 , and 7 F 1 → 7 F 6 . The luminescence characteristics were examined by photoluminescence (PL) and radioluminescence (RL). Both PL and RL confirmed that the optimum value at 2 mol% of Eu 2 O 3 concentration. Similarly, the luminescence efficiency of 2 mol% Eu 2 O 3 concentration compared with the BGO crystal equals 16.77%. As the concentration of Eu 2 O 3 increased, the experimental decay curve dropped while the energy transfers efficiency ( ɳET ) and the energy transfer parameter (Q) raised. Interestingly, the CIE of emission spectra under 393 nm (UV lamp) were reddish orange (0.64, 0.35). The branching ratio (β R ) was most significant at 612 nm, and the JO parameter trend was Ω 2 > Ω 6 > Ω 4 . Furthermore, all characterizations confirm its applicability in optical display devices.
optics