Abstract:The present work investigates the correlations between galvanic corrosion, intermetallic compound (IMC) formation, and the input of welding energy with respect to the initiation and propagation of micro-cracks in micropillars of resistant spot welding (RSW) joints between aluminum (Al) and steel. The present results indicate that, in the high welding energy region, Al was corroded first after 26 cycles of corrosion, and Al 5 Fe 2 IMC was corroded after 72 cycles of corrosion due to its high corrosion potential predicted by the calculations based on density functional theory (DFT) in terms of the Nernst equation. In comparison with the high welding energy region, less corrosion was observed in the middle welding energy region due to the thinner Al 5 Fe 2 IMC layer, a lower amount of Al 13 Fe 4 IMC in the Al matrix, and lower residual stress. Mechanical properties at different locations after various corrosion conditions were obtained using in situ compression tests, including the stress-strain responses and the strain rate sensitivity. The micropillars from the high welding energy region have a higher average yielding stress due to the thicker IMC layer than those from the middle welding energy region. The yielding stress decreases gradually with increasing corrosion cycles. Three conditions for crack initiation and propagation have been identified: firstly, for pillars from the high welding energy region before corrosion or the middle welding energy region (before or under the minimal corrosion conditions), the cracks initiate within the IMC layer; secondly, for pillars from the high welding energy region after 26 cycles of corrosion (under the moderate corrosion condition), cracks propagate at the Al/IMC interface; finally, for pillars from the high welding energy region after 72 cycles of corrosion (under the severe corrosion condition), the cracks initiate at the IMC/steel interface.

The Reliability Assessment of Au–Al Bonds Using Parallel Gap Resistance Microwelding

Al-clad Cu Bond Wires for Power Electronics Packaging: Microstructure Evolution, Mechanical Performance, and Molecular Dynamics Simulation of Diffusion Behaviors

Comparison of Interface Evolution of Ultrasonic Aluminum and Gold Wire Wedge Bonds During Thermal Aging

Metallurgical Behavior of Au/Al Bond Interface during High Temperature Storage of Ultrasonic Wedge Bonding

Brittle-to-ductile transition of Au2Al and AuAl2 intermetallic compounds in wire bonding

Growth of the nano-phase intermetallic compounds and its effect on mechanical behavior of Au80Sn20/CrMnFeCoNi solder joints during isothermal aging

Mechanical and Electrical Properties of Au-Al and Cu-Al Intermetallics Layer at Wire Bonding Interface

The aging characteristics of resistance rivet welded aluminum/steel joints

Effects of long-term thermal aging on the microstructure and mechanical behaviors of 16MND5/Alloy 152 dissimilar metal weld

Analysis of Degradation of Electromigration Reliability of Au-Al and OPM Wire Bonded Contacts at 250 °C Using Resistance Monitoring Method

Influence of accelerated corrosion on al/steel RSW joints by in situ compression tests

Calculation of Mechanical Properties, Electronic Properties, and Thermodynamic Properties of AuAl Crystal: First‐Principles Calculation

Comparison and mechanism of electromigration reliability between Cu wire and Au wire bonding in molding state

Comparison of Bond Interface Reaction in Al-Ni and Al-Au Systems Formed by Ultrasonic Wedge Bonding

A novel insight into Au-Au thermosonic flip chip joint under extreme thermal cycles: Defect characterization and failure analysis

Impact from IMC Thickness on the Reliability of Wire Bonding

Growth behavior of Cu/Al intermetallic compounds and cracks in copper ball bonds during isothermal aging

Investigation of the Mesoscale Damage Evolution Process of AA5754O Aluminum Alloy CMT Welded Joints

Microstructural and mechanical properties of Al–Mg–Si–Cu joint fabricated by rotary friction welding

Effect of thermal aging on microstructure, shear and mechanical shock failures for solder ball bonding joint

Thermal Reliability of Ag-8Au-3Pd Alloy Wire Bonds