Dielectric and Ferroelectric Properties of Bismuth-Layer High Curie Point Na0.5Bi4.5Ti4O15 Ceramics with Mg-doping
Can-Can Zhang,Jian-Xiong Zou,Lin-Hao Li,Qian Luo,Chao Ma,Lin Gui,Lu Qin,Peng Guo,Chun-Lei Liu,Yong Chen,Yi-Min Ding,Ling-Fang Xu
DOI: https://doi.org/10.1016/j.ceramint.2017.07.128
IF: 5.532
2017-01-01
Ceramics International
Abstract:As a new kind family of lead-free Na0.5Bi0.5TiO3 (NBT) ceramics, bismuth layer-structured ferroelectrics (BLSFs), Na0.5Bi4.5Ti4MgxO15+x and Na0.5Bi4.5Ti4-xMgxO15-x ceramics (with x = 0.04, 0.08) were artificially compounded by a conventional mixed oxide route. Under different sintering temperatures, we changed the Ti content of ceramics or Mg-doping on Ti-site in order to explore the ferroelectric and dielectric properties. XRD standard patterns of Na0.5Bi4.5Ti4MgxO15+x and Na0.5Bi4.5Ti4-xMgxO15-x (with x = 0.04, 0.08) proved that the materials were a single phase of BLSFs. By analysing the data of impedance spectra, we found that the Na0.5Bi4.5Ti4Mg0.04O15.04 ceramics sintered at 1100°C showed prominent dielectric properties with a dielectric constant of 1915.65 at 100kHz and a dielectric loss of 0.0020 at 1MHz, which were enhanced much compared with other samples. Meanwhile, the Curie temperature (Tc) of all samples were about 660°C. Moreover, the ferroelectric hysteresis loops of all the samples revealed that they were ferroelectric materials, which possessed a remanent polarization (2Pr) from 5.16 to 8.78µC/cm2 and a coercive field from 101 to 127.78kV/cm. The cross-section SEM showed that all samples had no c-axis orientation, whose grain distribution was more and more uniform and regular when activation energy (Ea) increased. The Ea can be calculated in the range of 1.10–1.47eV, which indicated they were dielectric ceramics. Consequently, the ceramics have the prospect of application in high-temperature capacitors and phase shifter field because of their high dielectric constant, low dielectric loss and wide operating temperature range.