Ferroelectric, electromechanical, and dielectric properties of (Na 0.5 Bi 0.5 ) 0.94 Ba 0.06 TiO 3 co-doped MnO 2 and La 2 O 3 lead-free ceramics

Qiang Li,Hairong Wang,Huiqing Fan,Changbai Long,Xiao Liu

DOI: https://doi.org/10.1007/s10853-013-7694-x

IF: 4.5

2013-01-01

Journal of Materials Science

Abstract:The modified (Na 0.5 Bi 0.5 ) 0.94 Ba 0.03 La 0.02 Ti 0.995 Mn 0.005 O 3 lead-free ceramics were prepared using a traditional solid-state reaction process, and their structures were characterized by X-ray diffraction, scanning electron microscope, and Raman spectroscopy, respectively. A double-like P–E loop was discussed at the room temperature for the co-doped ceramics by reason of the appearance of the anti-ferroelectric. The ferroelectric hysteresis loop and field-induced strain were studied at different temperatures. A large strain ( S 33 = 0.33 %, E = 50 kV/cm at 120 °C) was observed due to the transformation between ferroelectric and anti-ferroelectric phase at the phase transition temperature. Also, the depolarization temperature ( T d ) of the co-doped ceramics was determined from the pyroelectric current density versus temperature plots, which was consistent with the result from the position of dielectric loss’s peak as a function of temperature.