Ferroelectric properties and large electric field-induced strain of Eu<SUP>3+</SUP>-doped Na_0.5Bi_0.5TiO₃-BaTiO3 lead-free ceramics

Na Wu,Dongfang Pang,Tongxiang Liang,Xiang He

DOI: https://doi.org/10.1016/j.ceramint.2022.04.343

IF: 5.532

2022-01-01

Ceramics International

Abstract:Eu3+-doped lead-free piezoelectric ceramics, 0.937Na0.5Bi0.5_xEuxTiO3-0.063BaTiO3 (abbreviated as NBExT-BT, where x = 0, 0.003, 0.005, 0.01, 0.013, 0.015, 0.017, and 0.02), were synthesized using a conventional solidstate synthesis method. All the component samples were crystallized in a pure perovskite structure without a secondary phase. The introduction of Eu3+ caused the evident variation of the dielectric, ferroelectric and luminescence properties. The remanent polarization and coercive field of the pure NBT-BT are Pr -29.24 mu C/ cm2, Ec-39.33 kV/cm, respectively. The maximum of the remanent polarization Pr of -38.02 mu C/cm2 at room temperature and the highest dielectric constant of 6899 with a frequency of 1 kHz were obtained for NBE0.003TBT. The maximum bipolar strain Smax of -0.91% and the minimum of coercive field Ec -18.45 kV/cm were achieved by the NBE0.015T-BT, resulting from the formation of a double hysteresis loop. For all the components, Eu3+ doping stabilized the antiferroelectric phenomenon at high temperature. Furthermore, the polarized NBE0.015T-BT had the strongest fluorescence luminescence intensity as well as a fluorescence lifetime reaching 785.98 mu s.