Abstract:PEG/PMMA binder systems are among the most widely used water-soluble binders for ceramic injection molding. Binder-induced binder segregation in PEG/PMMA systems is mainly caused by the difference between crystallization temperature of PEG (below 50°C) and glass transition temperature of PMMA (~120°C). In this study, we have adopted the method of introduction of appropriate amount of PVP to reduce the binder-induced defects. A principle model was thus established for the suppression of PEG crystallization by PVP molecules. It was revealed that the mechanism by which PVP suppresses PEG crystallization is hydrogen-bonded formation between the carbonyl group of PVP and the hydroxyl groups of PEG molecules. This compresses the crystallization space of PEG molecules, and suppresses their crystallization. It was determined that the range of PVP content that can be safely removed via water debinding is 0–30wt/wt% PEGS. The incorporation of PVP could effectively enhance the homogeneity of the compact, reduce the size of pores formed after thermal debinding in the compact, promote densification, reduce defects after sintering and enhance the mechanical performance of the sintered bodies. Furthermore, the performance of the molded product was optimal when 20wt/wt% PEGS of PVP was added to the binder; the flexural strength and density of the resulting sintered body were 811MPa and 98.7%, respectively.

Study on PVB Binders Applied in Ceramic Injection Molding

Study on PVA/PEG water soluble binders applied in ceramics injection molding

Study Of Water-Debinding For Ceramic Parts By Injection Molding

Preparation of a novel water-soluble binders applied in ceramic injection molding and study on debinding process

Research On Sipm-Peg As Water-Soluble Binders Applied In Ceramic Injection Molding

Compatibility of Binder Systems for Water Extraction in Ceramic Injection Molding

Study of Thermal Degradation Mechanism of Binders for Ceramic Injection Molding by TGA-FTIR

Effects of PVP Incorporation on the Properties of Injection-Molded High-Performance Ceramics with PEG-based Binders

Mechanism of Thermal Debinding and Water Debinding for Ceramic Injection Molding

Study on the characteristics of injection molding green bodies of ZrO 2 ceramics

Application of POM in Catalytic Debinding of a Novel Ceramic Injection Molding Feedstock

Water Debinding for Zirconia Powder Injection Molding

Study on the characteristics of injection molding green bodies of ZrO2 ceramics

A new method of debinding for injection molding of ceramics - Supercritical carbon dioxide extraction

Study of Water-Debinding for Ceramic Parts with Thick Cross-Section by Injection Molding

Effect of the debinding method on the properties of injection molding ceramics

Theory and Practice of Rapid and Safe Thermal Debinding in Ceramic Injection Molding

Effects of the Binder Compositions on the Homogeneity of Ceramic Injection Molded Compacts

The thermal debinding of soluble binders in injection molded zirconia ceramic from room temperature to 250°C

Effects of Different Backbone Binders on the Characteristics of Zirconia Parts Using Wax-Based Binder System Via Ceramic Injection Molding