Abstract:PEG/PMMA binder systems are among the most widely used water-soluble binders for ceramic injection molding. Binder-induced binder segregation in PEG/PMMA systems is mainly caused by the difference between crystallization temperature of PEG (below 50°C) and glass transition temperature of PMMA (~120°C). In this study, we have adopted the method of introduction of appropriate amount of PVP to reduce the binder-induced defects. A principle model was thus established for the suppression of PEG crystallization by PVP molecules. It was revealed that the mechanism by which PVP suppresses PEG crystallization is hydrogen-bonded formation between the carbonyl group of PVP and the hydroxyl groups of PEG molecules. This compresses the crystallization space of PEG molecules, and suppresses their crystallization. It was determined that the range of PVP content that can be safely removed via water debinding is 0–30wt/wt% PEGS. The incorporation of PVP could effectively enhance the homogeneity of the compact, reduce the size of pores formed after thermal debinding in the compact, promote densification, reduce defects after sintering and enhance the mechanical performance of the sintered bodies. Furthermore, the performance of the molded product was optimal when 20wt/wt% PEGS of PVP was added to the binder; the flexural strength and density of the resulting sintered body were 811MPa and 98.7%, respectively.

Water Debinding for Zirconia Powder Injection Molding

Study Of Water-Debinding For Ceramic Parts By Injection Molding

Mechanism of Thermal Debinding and Water Debinding for Ceramic Injection Molding

Study of Water-Debinding for Ceramic Parts with Thick Cross-Section by Injection Molding

Optimization of the compositions of PEG/PMMA binder system in ceramic injection moulding via water-debinding

Water-Soluble Binder System Based On Poly-Methyl Methacrylate And Poly-Ethylene Glycol For Injection Molding Of Large-Sized Ceramic Parts

Optimisation of compositions of PEG/PMMA binder system in ceramic injection moulding via water debinding

Compatibility of Binder Systems for Water Extraction in Ceramic Injection Molding

Injection Molding of Zirconia Ceramics Using Water-Soluble Binder

Surface Modification and Water Debinding in Zirconia Powder Injection Molding

Dynamics of water debinding in ceramic injection moulding

Novel Fabrication of Injection-Moulded Ceramic Parts with Large Section Via Partially Water-Debinding Method

The thermal debinding of soluble binders in injection molded zirconia ceramic from room temperature to 250°C

Study on PVA/PEG water soluble binders applied in ceramics injection molding

Effects of PVP Incorporation on the Properties of Injection-Molded High-Performance Ceramics with PEG-based Binders

Preparation of a novel water-soluble binders applied in ceramic injection molding and study on debinding process

Research On Sipm-Peg As Water-Soluble Binders Applied In Ceramic Injection Molding

Effect of the debinding method on the properties of injection molding ceramics

Solvent Debinding Behavior of Zirconia Powder Injection Molding

A new method of debinding for injection molding of ceramics - Supercritical carbon dioxide extraction