Preparation and Electrical Properties of SmBaCuFe1 xCoxO5+delta Oxide Thermoelectric Materials

CC Zeng,YH Lin,JL Lan,M Li,Y Shen,CW Nan

2015-01-01

Rare Metal Materials and Engineering

Abstract:The single phase perovskite SmBaCuFe1-xCoxO5+delta(x=0, 0.3, 0.5, 0.7) ceramics have been prepared through a sol-gel method followed by solid-state sintering reaction. Relative density of all samples are above 90%. The electrical conductivity and Seebeck coefficient have been tested in the temperature of 303 similar to 1023 K. The electrical conductivity increases with increasing x, leading to a drastic increase from 0.75 to 41.24 S/cm at 1023 K. The activation energy significantly decreases from 0.38 eV down to 0.23 eV through fitting relationship between resistivity and temperature. The optimal cobalt doping content x is 0.3, when the SmBaCuFe0.7Co0.3O5+delta sample shows the maximum power factor (PF) of 0.241 mu W.cm(-1.)K(-2) at 1023 K