Antibacterial Properties of Pure Magnesium Made on Biological Film Treated by Ultrasonic Micro-arc Oxidation Phytic Acid with Chemical Galvanizing

LIU Ji-guang,SONG Jia-qi,LI Mu-qin,JIN Peng-li,WEI Fang-hong

DOI: https://doi.org/10.11933/j.issn.1007-9289.2016.06.012

2016-01-01

China surface engineering

Abstract:Aiming for postoperative infection caused by medical metallic implant materials, and based on the treatment process of ultrasonic micro-arc oxidation (UMAO) in the pure magnesium, Zn was introduced to profit antibacterial properties and biological activity of the films using the chemistry galvanized method. In order to explore the effect of antibacterial properties with different Zn contents on the film. Morphologies and organization structure were analyzed by XRD, SEM and EDS methods, and the laminating method was used to test antibacterial properties. The results show that as the galvanizing time grow, the membrane pores on the surface are reduced, the membrane becomes denser, Zn content increases, and the corrosion resistance performance is improved. Zn content has a direct effect on antibacterial performance of the film, while the chemical galvanized duration is equal to 5 min, Zn content is 1.50%, and the antibacterial rate for E.coli and S.aureus is as high as 99%, which is obviously greater than the galvanized group with 1 min and galvanized group with 3 min when compared. Antibacterial properties of the film of pure magnesium ultrasonic micro-arc oxidation phytic acid are enhanced by chemical galvanizing, as Zn content increases. When chemical galvanized for 5 min, the film develops a relatively stronger antibacterial function.