Numerical modelling of deformation prediction for laser-assisted laser peen forming

Mingsheng Luo,Yongxiang Hu

2017-01-01

Abstract:Introduction Laser peen forming (LPF) is a forming technique using laser-induced plasma to impact the workpiece spot-by-spot and forming the metal sheet into a specified curvature. It is a complex physics process including laser ablation, shock wave propagation, material yielding and deformation accumulation. A high-intensity short-pulsed laser irradiates on the surface of the workpiece, as a result, high pressure plasma generates on the surface of the workpiece in the confinement of water. In the impact of high pressure plasma, the shock pressure generates and spreads to the depth direction. The amplitude of the shock wave arrives at 1-10 GPa and the time duration is around 100 nanoseconds, as a consequence LPF is a high-dynamic response process due to the laser shock process. When the shock wave exceeds the Von Mises stress of materials, the workpiece in the shock zone yields and generates plastic strain. After laser scanning over the workpiece surface, the deformation is accumulated with the expanding of the plastic zone, resulting in the workpiece bending into a small curvature convex shape. In order to overcome the difficulty of improving the pulse energy, laser-assisted laser peen forming(LALPF) was proposed by Hu et al. [1] to improve the bending capability. LALPF adapted CW laser heating to increase the deformation. Laser heating plays an assisted role in softening the material and altering the stress state of material during LALPF. Simutationly, the back surface of the workpiece is heating by continuous wave (CW) laser which is coaxial with the pulsed laser. The material absorbs the CW laser energy resulting in high temperature field in the local area. The local high temperature decreases the yield strength, inducing thermal stress even plastic thermal strain owing to the nonuniform expansion of material. Thus, lager and deeper plastic strain is generated in the laser shock process and the deformation of the workpiece increase compared with the LPF in room temperature.