Bi ( Mg 2 / 3 Nb 1 / 3 ) O 3-BaTiO 3-BiFeO 3 PbO-free Piezoelectric Ceramics

Shunsuke Murakami,Dawei Wang,Amir Khesro,Antonio Feteira,Derek C. Sinclair,Ian M Reaney

2017-01-01

Abstract:Pb(Zr,Ti)O3 (PZT) has been widely applied in piezoelectric devices over the past few decades. However, concerns about environmental and health problems are growing because lead has significant toxicity [1]. BaTiO3-BiFeO3 (BT-BF) based materials are promising candidates for lead free piezoelectric materials. Lee reported that BT-BF based ceramics have high piezoelectric coefficient, d33 = 402 pC/N coupled with a high TC = 454oC after quenching [2]. However, there are challenges in applying quenched BT-BF ceramics for industrial applications such as poor mechanical reliability. Moreover, BT-BF ceramics lack the high temperature reliability needed for high strain/field piezoelectric applications such as fuel injectors for automotive engines. It has been suggested that the high leakage current results from either loss of Bi or formation of Fe as opposed to Fe during sintering and many researchers reported that some dopants alleviate these problems. However, the detailed mechanism of the dopant effects in BT-BF ceramics is still unclear because both acceptor and donor dopants have been reported to improve the resistivity of BT-BF ceramics [4, 5]. The aim of our work is to investigate the role of dopants and thus improve the piezoelectric properties in BT-BF based ceramics. To this end, we have studied (Mg2/3Nb1/3) as a self-compensated dopant in BT-BF ceramics within the solid solution (1-x-y)Bi(Mg2/3Nb1/3)O3-(x)BaTiO3-(y)BiFeO3. (Mg2/3Nb1/3) successfully unlocks the potential of BT-BF ceramics and (1-x-y)Bi(Mg2/3Nb1/3)O3-(x)BaTiO3-(y)BiFeO3 exhibits high strain and low temperature dependence of strain.