Enhanced high-temperature piezoelectric properties of Bi(Zn0.5Ti0.5)O3-modified BiFeO3–BaTiO3 ceramics
Tong-Guang Dai,Yu-Cheng Tang,Le-Tian Xie,Hezhang Li,Xiao-Qi Gao,Aizhen Song,Jun Pei,Huan Liu,Bo-Ping Zhang
DOI: https://doi.org/10.1007/s10853-023-08614-0
IF: 4.5
2023-06-20
Journal of Materials Science
Abstract:This paper reports enhanced high-temperature piezoelectric properties of Bi(Zn 0.5 Ti 0.5 )O 3 -modified BiFeO 3 -BaTiO 3 (BF–BT- x BZT) ceramics prepared by two-step sintering method. The resultant ceramics show a symmetrical transition from a rhombohedral–pseudo-cubic ( R-PC ) phase coexistence to main PC phase with the increase of x , whose R-PC fraction (C R /C PC ) is 53.3/46.7, 52.9/47.1, 50.2/49.8, 27.4/72.6, 15.3/84.7 when x = 0, 0.005, 0.01, 0.03, 0.05, respectively. The modification of BZT inhibits the grain growth, reduces the leakage current and gradually drives ferroelectric to relaxor transition. Optimal piezoelectric properties: d 33 = 193 pC N −1 , P r = 20.6 μC cm −2 , T C = 503 °C and k p = 36% achieved at x = 0.01 composition, which is due to the synergistic effect of an appropriate C R /C PC ratio, improved insulation and good polarization performance. In addition, the depolarization temperature T d is close 280–312 °C, and the high-temperature d 33 further increases to 286–347 pC N −1 , which shows a good application prospect of lead-free piezoceramics at high temperature. Our work also confirms that the addition of (Zn 0.5 Ti 0.5 ) 3+ and two-step sintering method are an effective and convenient strategy to improve the high-temperature electrical performance of BiFeO 3 –BaTiO 3 based lead-free ceramics.
materials science, multidisciplinary