Abstract:Novel composites (MOF-5 and Cu-BDC) based on economically activated carbon have been developed to investigate methane adsorption capacity for ANG applications. The composites were synthesized by adding MOFs precursor in two different weight percent (10% and 40%) to commercial activated carbon under solvothermal conditions (110-120°C). The synthesized adsorbents were characterized by FT-IR, XRD, SEM, EDS, and BET techniques to gather information about their crystallinity, morphology, and specific surface area. A methane uptake measurement system based on the volumetric method was made to obtain methane adsorption capacity on each composite. Then, the amount of methane adsorption for each one was calculated, and the experimental data were compared with different isotherm adsorption models appropriate for gas adsorption, including Langmuir, Freundlich, and Dubinin-Radushkevich. This comparison showed that the best fitting belonged to the Langmuir isotherm model. Also, stability and kinetic studies were done for two MOF-540% @AC and Cu-BDC40% @AC composites. In the kinetics study, experimental data were compared and analyzed in terms of pseudo-first order, pseudo-second order, and intraparticle diffusion models. The kinetics study showed that methane adsorption happens very fast on the synthesized adsorbents. The amount of methane adsorption at 35 bar and room temperature for pure activated carbon was specified as 4.32 mmol/g. The 10% and 40% of Cu-BDC with activated carbon are 5.59 mmol/g and 6.85 mmol/g, respectively. The capacity of MOF-510% @AC and MOF-540% @AC composites were obtained at 5.9 mmol/g and 7.3 mmol/g, respectively. Increasing methane uptake (70%) was obtained by adding 40 wt.% of MOF-5 to commercial activated carbon.

Thermo-Gravimetric Analysis of Methane Catalytic Decomposition over Activated Carbons

Thermo-Gravimetric Analysis of Methane Catalytic Decomposition over Carbon Blacks

Study on carbonization of lignin by TG-FTIR and high-temperature carbonization reactor

Key factors that affect catalytic activity of activated carbon-based catalyst in chemical looping methane decomposition for H2 production

Mechanism of activated carbon-catalyzed methane decomposition process for the production of hydrogen and high-value carbon

Influence of Tectonically Deformed Coal-Based Activated Carbon and Its Surface Modification on Methane Adsorption

Hierarchical Pore Structure of Activated Carbon Fabricated by CO2/microwave for Volatile Organic Compounds Adsorption

Synthesis of micro-mesoporous hierarchical structure of coal-based activated carbon and its effect on methane adsorption

Photocatalytic Degradation of Gaseous 1,2-Dichlorobenzene over TiO2/AC Photocatalysts

Effect of Surface Area and Micropore Volume of Activated Carbons from Coal by KOH, NaOH and ZnCl2 Treatments on Methane Adsorption

The Chemical Nature of Carbonaceous Deposits and Their Role in Methane Dehydro-Aromatization on Mo/MCM-22 Catalysts

Carbonaceous Deposition on Mo/HMCM-22 Catalysts for Methane Aromatization: A TP Technique Investigation

Protrusions induction by carbon black on surface of activated carbon to enhance its catalytic activity

Structure Characteristics and Removal Behavior of the Deposited Carbon on Ni-Al2O3 Catalyst for CO2 Reforming of CH4

Spontaneous Combustion Risk of Coal-based Activated Carbon

Dynamical Characteristics of Methane Adsorption on Monolith Nanometer Activated Carbon

Catalytic methane decomposition on CNT-supported Fe-catalysts

An analysis of the carbonization process of coal-based activated carbon at different heating rates

Effect of activated carbon catalyst on the cracking of biomass molecules into light hydrocarbons in biomass pyrolysis

Microporous MOF-5@AC and Cu-BDC@AC Composite Materials for Methane Storage in ANG Technology

The Reactivity of Surface Active Carbonaceous Species with CO2 and Its Role on Hydrocarbon Conversion Reactions