Evolution of austenite dislocation density during hot deformation using a physical dynamic recrystallization model

Zhou,Peng,Ma,Qingxian

DOI: https://doi.org/10.1007/978-3-319-52132-9_71

2017-01-01

Abstract:A new model to predict the dislocation density evolution of 30Cr2Ni4MoV steel during hot deformation was proposed in this study. Hot compression of 30Cr2Ni4MoV steel was carried out on Gleeble 1500 at different temperatures and strain rates. A series of flow curves was obtained and the experimental dislocation density evolution was derived from the experimental flow curves. Based on the obtained flow curves, the dependences of yield stress, critical stress and strain of dynamic recrystallization and the saturation stress on temperature and strain rate were determined. Two sets of dislocation density equation were derived from the experimental flow curves: (I) a dislocation density relation describing the grains in which dynamic recovery took place only; and (II) an average dislocation density expression pertaining to the recrystallized grains. All the parameters needed for the determination of the dislocation equations were calculated and expressed as a function of strain, temperature and strain rate. A physically realistic and practical kinetics model of dynamic recrystallization was determined with the aid of the above relations. Finally, the dependence of the dislocation density on strain, deformation temperature and strain rate was determined and the predicted results agreed well with the experimental results.