Abstract:Sr2SiO4:Eu2+ phosphors were synthesized by a conventional solid state reaction method. After a low amount of nitrogen (similar to 1 mol% of oxygen) was incorporated to modify the local coordination environment of Eu2+, the phosphor showed a single intense broad band emission centered at 625 nm under blue light (453 nm) excitation, and three emission bands (480, 555 and 625 nm) under ultraviolet irradiation. The incorporation of nitrogen was confirmed by X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy (FT-IR) and absorption spectroscopy. 480 and 555 nm emissions originated from Eu2+ ions occupying the Sr(I) sites and Sr(II) sites in the Sr2SiO4 crystal, respectively, while 625 nm emission originated from the nitrogen coordinated Eu2+ ions. The local coordination structure around Eu2+ ions in the red phosphors was analyzed with the aid of density functional theory based first principles calculations. The analysis showed that nitrogen should preferentially substitute the O5' sites around Eu2+ in Sr(II) sites, which agreed fairly well with the experimental results from the X-ray absorption fine structure (XAFS) and the electron paramagnetic resonance (EPR) spectra. The electronic structure analysis confirmed the lowered center of gravity of Eu 5d energy states and the broadened Eu 4f energy states, which are due to the tightened coordination environment and the hybridization of the 4f states of Eu and 2p states of nitrogen-oxygen, leading to a red emission. The novel nitrogen modified Sr2SiO4:Eu2+ could serve as a full color phosphor for near-UV LEDs or a red-emitting phosphor for blue LEDs.

Preparation and Luminescence Properties of the Red-Emitting Phosphor (sr1–xcax)2si5n8:Eu2+ with Different Sr/Ca Ratios

Synthesis, Crystal Structure, and Luminescence Properties of Tunable Red-Emitting Nitride Solid Solutions (Ca1-Xsrx)(16)si17n34:Eu2+ for White Leds

Red-emitting Oxonitridosilicate Phosphors Sr2SiNzO4−1.5z:Eu2+ for White Light-Emitting Diodes: Structure and Luminescence Properties

Preparation of (Sr1- xCax)2Si5N8 /Eu2+ solid solutions and their luminescence properties

Preparation of (Sr[sub 1−x]Ca[sub x])[sub 2]Si[sub 5]N[sub 8]∕Eu[sup 2+] Solid Solutions and Their Luminescence Properties

Synthesis of Nitridosilicate Casr1-Xeuxsi5n8 (X=0-1) Phosphor by Calcium Cyanamide Reduction for White Light-Emitting Diode Applications

Preparation of Sr1−xCaxYSi4N7:Eu2+solid Solutions and Their Luminescence Properties

Synthesis, structure, and luminescence properties of SrSiAl<sub>2</sub>O<sub>3</sub>N<sub>2</sub>:Eu<sup>2+</sup> phosphors for light-emitting devices and field emission displays

Syntheses and Photoluminescence Properties of Sr2Si5N8:Eu2+ Phosphors

Characterization and Luminescence Properties of Sr2Si5N8:Eu2+ Phosphor for White Light-Emitting-diode Illumination

Synthesis and Photoluminescent Properties of Sr2Si5N8:Eu2+ Red Phosphors for White Light-Emitting Diodes

Luminescence properties of nitride red phosphor for LED

Li 2 SrSi 2 N 4 :Eu 2+ : Electronic structure and luminescence of a red phosphor

Intense Red Light Emission Of Eu3+-Doped Sr3b2sio8 For White Light-Emitting Diodes

Synthesis and Luminescence Properties of Orange–Red‐Emitting M2Si5N8:Eu2+ (m=ca, Sr, Ba) Light‐Emitting Diode Conversion Phosphors by a Simple Nitridation of MSi2

Synthesis and Photoluminescence Properties of Sr(2)Si(5)N(8):Eu(2+) Red Phosphor by A Gas-Reduction and Nitridation Method

Preparation, Structure and Luminescence Properties of Deep Red Phosphors SrSiN2:Eu2+

Synthesis and Luminescence Properties of Red-Emitting M 2 Si 5 N 8 :Eu 2+ -Based(m=ca,sr,ba) Phosphors by a Simple Nitrate Reduction

Preparation of Sr1−xCaxLiAl3N4:Eu2+ Solid Solutions and Their Photoluminescence Properties

Structure and Luminescence Properties of Sr-rich Phase (Ca,Sr)AlSiN<sub>3</sub>:Eu<SUP>2+</SUP> Orange Phosphors

Modification of the coordination environment of Eu2+ in Sr2SiO4:Eu2+ phosphors to achieve full color emission