Abstract:The need for 2219 aluminum alloy and 2195 Al–Li alloy dissimilar friction stir welding (FSW) arises as the conventional 2219Al alloy was gradually replaced by the novel 2195Al alloy in fabrication of fuel tanks. However, the systematic investigation about the effect of welding parameters and material positioning on the microstructure evolution and mechanical properties of dissimilar FSW 2219Al/2195Al joints is lacking. In the present study, 2219Al-T8/2195Al-T8 plates were subjected to FSW under rotation rates of 800–1200 rpm and welding speeds of 200–800 mm min −1 with placing 2219Al-T8 alloys on the advancing side (AS) and retreating side (RS), respectively. The results showed that sound FSW joints were obtained under all the welding conditions. Welding parameters and material positioning affected the joint strength and fracture failure behavior. The FSW thermal cycle resulted in low hardness zones (LHZs) on both the 2219Al-T8 and 2195Al-T8 sides. The LHZ on the 2219Al-T8 side, characterized by partial coarsening of θ ′ (Al 2 Cu) precipitates and dissolution of the residual precipitates, showed the minimum hardness in the entire FSW joints. When 2219Al-T8 alloy was placed on the AS, the LHZ on the 2219Al-T8 side experienced higher peak temperature, and therefore more dissolution of θ ′ than that on the RS, thereby obtaining higher tensile strength. The tensile strength of the FSW joints at room temperature and − 196 °C largely increased as the welding speed increased from 200 to 400 mm min −1 . The FSW joints presented much higher tensile strength at − 196 °C than that at room temperature under the identical welding parameters and material position. The FSW joints fractured along the LHZ on the 2219Al-T8 side during tension. For the bending testing, the up and down bending failure angles were about 91–117° and 88–109°, respectively, with the weak zone appearing in "S" line or HAZ on the 2195Al-T8 side.

Realization of ODS-Cu/T91 Tube-to-tube Joining with Rotary Friction Welding

Tungsten Joining with Copper Alloy and Its High Heat Load Performance

Characterization of Ductile Nano-Tic Dispersed V4Cr4Ti/RAFMs Solid Diffusion Joint for Nuclear Fusion Reactor Application

Intergrowth Bonding Mechanism and Mechanical Property of Linear Friction Welded Dissimilar Near‐Alpha to Near‐Beta Titanium Alloy Joint

Microstructural response at the interface and its effect on the fatigue fracture behavior of rotary friction welded dissimilar titanium alloys: Ti–5Al–2Sn–2Zr–4Mo–4Cr (Ti17) and Ti–6Al–2Sn–4Zr–2Mo (Ti6242)

Microstructure and texture distribution in the bonding interface of Cu/Al composite tube fabricated by explosive welding

Development of High Impact Toughness Cu/ODS-Cu Joints Using HIP Bonding Process for the Preparation of W/Cu/ODS-Cu Monoblock Divertor

Interface Microstructure and Numerical Simulation Investigations of Ni/TC18 Composite Tube Fabricated by Explosive Welding

Stable bonding of W and ODS steel fabricated by TLP diffusion technology through inserting a novel composite interlayer Zr/Cu

Friction Welding of ETP-Cu Plate to SS304L Round Bar: An Experimental Study on Asymmetrical Dissimilar Metal Joints

Microstructural and Performance Analysis of TP304H/T22 Dissimilar Steel Welded Joints

Quasi-equal Strength and Toughness Matching Rail Steel Joint Obtained Via Friction Welding below Ac1 Temperature

Quasi-equal strength and toughness matching rail steel joint obtained via friction welding below A c1 temperature

Effect of Different Welded Structures on Mechanical Properties of TA2 Tube-to-Tubesheet Joints

High-strength Diffusion Bonding of Oxide-Dispersion-strengthened Tungsten and CuCrZr Alloy Through Surface Nano-Activation and Cu Plating

Dissimilar friction stir welding of 2219-T8 and 2195-T8 aluminum alloys: part I—microstructure evolution and mechanical properties

A novel dynamic self-constrained explosive welding method for manufacturing copper-steel bimetallic tube

Diffusion bonding and interface structure of advanced carbide-dispersion-strengthened Cu and oxide-dispersion-strengthened W

Microstructure, Corrosion and Mechanical Properties of Medium-Thick 6061-T6 Alloy/T2 Pure Cu Dissimilar Joints Produced by Double Side Friction Stir Z Shape Lap-Butt Welding

Transient thermal shock and helium ion irradiation damage behaviors of ODS-W/CuCrZr joints

Microstructure, mechanical and fracture properties of friction stir welded 2195 Al-Li alloy joints