Potentiometric Sensor Based on Chromium Vanadate Sensing Electrode for High Temperature Ammonia Detection
Chao Wang,Yimin He,Hongming Liu,Bin Yang,Jingxin Wang,Hanyu Yu,Feng Xia,Jianzhong Xiao
DOI: https://doi.org/10.1149/1945-7111/abf4b1
IF: 3.9
2021-04-01
Journal of The Electrochemical Society
Abstract:Mixed-potential sensors using CrVO 4 sensing electrodes were prepared for monitoring ammonia at high temperatures. NH 3 sensitivity for the sensors sintered at 800 °C, 850 °C and 900 °C were −56.5, −75.0 and −32.1 mV/decade respectively for the NH 3 above 10 ppm. High sintering temperature strengthens the bond of electrode and electrolyte, thus increasing the amount of TPB sites. Thinner electrode weakens the heterogeneous catalytic consumption of NH 3 . More reaction sites combined with higher NH 3 concentration result in greater sensitivity for 850 °C-sintered sensor. 900 °C sintering leads to decomposition of CrVO 4 into Cr 2 O 3 and V 2 O 5 , which exhibits low NH 3 sensitivity. In operating temperature range of 500 °C–600 °C, NH 3 detection limit is 2 ppm. The sensor shows the biggest responses at 500 °C, but the optimum NH 3 sensitivity of −75.0 mV/decade was obtained at 550 °C for the concentrations higher than 10 ppm. For the oxygen of 4–10 vol %, response is less affected by the change of oxygen content, the influence of water vapor with content of 5–6 vol % could also be ignored. The characteristics of high NH 3 selectivity, sensitivity, long-term stability and anti-interference performances indicate that it is meaningful to use CrVO 4 for ammonia detection in exhaust.
electrochemistry,materials science, coatings & films