Abstract:CFRP strengthened specimens geometry and loading procedure for the fatigue tests. Carbon fiber‐reinforced polymer (CFRP) is increasingly used to improve the fatigue behavior of damaged steel structures due to its advantages, including high strength and convenient processing. However, several issues, such as the effects of the adhesive property and CFRP arrangement, still need to be studied. In this study, a total of 20 single‐cracked steel specimens were tested under fatigue load, including two unstrengthened specimens, six single‐sided strengthened specimens, and 12 double‐sided strengthened specimens. The failure mode, fatigue life, crack propagation pattern, and interface damage development were obtained from experiments. The results show that epoxy resin structural adhesives (adhesives Araldite 420 and J133C) have the best bonding properties with CFRP. For the conventional epoxy adhesives, Araldite 420 and J133C can considerably improve fatigue life, which increased by more than 44.84 times to unstrengthened specimens. CFRP plate strengthening can significantly improve the fatigue life of single‐edge cracked steel plates. For the double‐sided strengthened specimens, the fatigue life can be improved by 6.93–44.84 times that of unstrengthened specimens. For the single‐sided, the fatigue life can be improved by 2.24–2.77 times. Properties of epoxy adhesive have a more significant effect on fatigue life compared to the thickness of the CFRP plate due to debonding. Highlights Ductile epoxy adhesives are most conducive to improving the fatigue behavior of CFRP strengthened steel plates. The fatigue life of steel plates can be improved by increasing the thickness of CFRP plates and using double‐sided CFRP strengthening. Interface debonding is the main failure mode of CFRP plates strengthening single‐edge cracked steel plates under fatigue.

Enhancing fatigue performance of damaged metallic structures by bonded CFRP patches considering temperature effects

Experimental study on dynamic behavior of CFRP-to-steel interface

Study on thermal effects on fatigue behavior of cracked steel plates strengthened by CFRP sheets

Fatigue performance and parameter optimization of CFRP-reinforced steel plate considering elevated temperature

Fatigue Damage Tolerance of CFRP/Al Adhesive Joints with Thermal Effects

Fatigue performance of carbon fiber‐reinforced polymer strengthened single‐edge cracked steel plates: Effects of adhesive property and CFRP arrangement

Fatigue behaviour of cracked steel plates reinforced with uhm cfrp laminate

Fatigue Behaviour of Cfrp Strengthened Steel Plates with Different Degrees of Damage

Experimental Study on Repair of Steel Plate with Different Damage Degrees Subject to Fatigue Loading

Tests On Cracked Steel Plates With Different Damage Levels Strengthened By Cfrp Laminates

State-of-the-art on Fatigue Behavior of Steel Structures Strengthened with Carbon Fibre Reinforced Polymer Materials

Fatigue behavior and digital image correlation monitoring of steel plates with mixed-mode edge cracks repaired with CFRP materials

Discussion of “fatigue Behavior of Cracked Steel Plates Strengthened with Different CFRP Systems and Configurations” by Hai-Tao Wang, Gang Wu, and Jian-Biao Jiang

Experimental Study on Fatigue Performance of Adhesively Bonded Anchorage System for CFRP Tendons

An Experimental Study on Fatigue Characteristics of CFRP-steel Hybrid Laminates

Experimental study of the fatigue performance of steel beams strengthened with different fiber reinforced polymers

Experimental Study on Fatigue Behavior of Tensile Steel Plates Strengthened with CFRP Plates

Fatigue Life of CFRP Laminate Strengthened High-Strength Steel Plates under Fatigue Loadings

Fatigue Behavior of Cracked High-Strength Steel Plates Strengthened by CFRP Sheets

Experimental study on mixed-mode fatigue behavior of center cracked steel plates repaired with CFRP materials

Experimental Study on Interfacial Bond Behavior between CFRP Sheets and Steel Plates under Fatigue Loading