Expansion of Multifunctionality of Non-Stoichiometric Manganite Ceramics Owing to Post-Annealing: Effect of High Pressure and Electrochemical Studies
Zhiwei Gong,Wei Xu,N.A. Liedienov,D.S. Butenko,I.V. Zatovsky,Ziyu Wei,Quanjun Li,Bingbing Liu,A.V. Pashchenko,G.G. Levchenko
DOI: https://doi.org/10.2139/ssrn.4087340
2022-01-01
SSRN Electronic Journal
Abstract:Prospects for the use of manganites in various areas of modern technologies require comprehensive studies of their physical and chemical properties. La 0.9 Mn 1.1 O 3 (LMO) ceramics were synthesized at annealing temperature t ann = 1150 ℃ with further post-annealing at 1250, 1350, and 1450 ℃. They have been studied comprehensively using XRD, SEM, EDS, thermogravimetric, magnetic under high pressure, and electrochemical methods. As the t ann increases, the crystal structure symmetry changes from the rhombohedral R -3 c to the monoclinic P 21/ c type, the crystallite size and concentration of chemical defects increase, and the tolerance factor reduces. The post-annealing, on one hand, leads to a dramatic reduction of the magnetic entropy change –Δ S M max from 3.50 to 0.75 J/(kg⋅K) under 2 T and Curie temperature T C from 227 to 113 K with an increase in the t ann . This is due to the weakening of both the double-exchange (DE) and multiple DE interactions by the increased content of chemical defects. On the other hand, an external hydrostatic pressure works oppositely enhancing DE interactions and reducing the disorder. The saturation of the –Δ S M max and T C is achieved already at around 0.4 GPa. The LMO-1150 exhibits the best magnetocaloric characteristics to compare with other studied samples. Moreover, the electrochemical characteristics of the LMO materials as electrocatalysts for overall water splitting (OER process) and features of their transformation in different 0.5 M K 2 SO 4 , 0.5 M K 2 HPO 4 , and 0.1 M K 2 B 4 O 7 electrolytes have been studied thoroughly. After electrocatalysis, the magnetization M decreases and the T C remains the same indicating the persistence of the DE. All samples show the best electrochemical performance in the 0.5 M K 2 HPO 4 media. The obtained results demonstrate the ways for controlling magnetocaloric parameters of the LMO ceramics at changing the internal and external conditions, as well as an evaluation of the possibilities for their OER applications in electrocatalysts.