Abstract:This study examines the effect of cooling rate (specifically at 2.3, 3.4, 9.8 and 24.1 K/s as) on the microstructure and mechanical properties of an Al-5.0Mg-3.0Zn-1.0Cu (wt.%) alloy casted through a step-like iron mold. This study was performed in as-cast and T6-treated (470 degrees C x 24 h + 150 degrees C x 16 h) conditions. An examination of the as-cast microstructure shows that when the cooling rate increases from 2.3 to 24.1 K/s, the average secondary dendrite arm spacing decreases from 43.0 to 19.0 mu m, and that the average width of the T-Mg-32(AlZnCu)(49) phase also decreases from 6.7 to 4.0 mu m. The solution treatment has an impact on dissolving most of the T phases and aging treatment results in the formation of fine precipitates in matrix. The examinations of precipitates under different cooling rates show that a higher cooling rate promotes the transformation from the GP II zone to eta' phase and also keeps a higher concentration of Mg and Zn suspended in the alloy matrix. The results of tensile tests show that the strength and elongation of as-cast alloys are improved slightly by applying a higher cooling rate, and that of T6-treated alloys improved more significantly, especially for elongation (from 6.1% to 10.6%) and yield strength (from 402.5 to 441.9 MPa). The refinements of alpha-Al and Al3Fe phases are attributed to the significant increase of elongation for T6-treated alloys. Moreover, cooling rate regulates the yield strength by mainly affecting precipitation strengthening and the relative mechanisms are discussed. Overall, these results show that Al-5.0Mg-3.0Zn-1.0Cu cast alloy can exhibit a strength of 450 MPa, a high ductility of 10%, and can become one of high performance cast aluminum alloys. (C) 2019 Elsevier B.V. All rights reserved.

Effect of Zn/Mg/Cu Additions on Hot Cracking Tendency and Performances of Al-Cu-Mg-Zn Alloys for Liquid Forging

Fabrication and Properties of Al-Cu-Mg-Zn Series Alloys with Low Hot Cracking Tendency for Liquid Forging

Effect of Cu Additions on Microstructure, Mechanical Properties and Hot-Tearing Susceptibility of Mg-6Zn-0.6Zr Alloys

Effects of Zr and Mg alloying on microstructure and properties of Cu-Cr-Si alloys

Study on the effect of enhanced magnesium and copper contents on microstructure and property of Al-Zn-Mg-Cu alloys with high zinc element content during fabrication processes

Effect of Zn/Mg Ratio on Microstructure and Properties of Cold Extruded Al-xZn-2.4Mg-0.84Cu-0.2Zr-0.25Ti Aluminum Alloy

Microstructure and Mechanical Properties of Al-5Cu-4.5Mg-2.5Zn Squeeze Cast Alloy

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Effect of Zn/Mg ratio on T6 state microstructure and properties of Al-xZn-2.6Mg-0.94Cu-0.2Zr-0.8Ti cold extruded aluminum alloy

Microstructure, Mechanical Properties and Corrosion Behaviors of Al–Li–Cu–Mg–Ag–Zn Alloys

Experimental Investigation and Simulation Assessment on Fluidity and Hot Tearing Susceptibility of Al-Li-Cu-X Alloy: the Role of Microalloying Elements

Effect of Forging on Microstructure and Properties of Al-9Si-5Cu-0.2Zr-0.1Sr-0.16Ti-0.1Ce Cast Aluminum Alloy

Effect of Zn Addition on Microstructure and Mechanical Properties of Mg–9Gd–3Y–0.5Zr Alloy

Microstructures and Mechanical Properties of Hot-extruded Mg-6Zn-xCu-0.6Zr(x=0,0.5,1.0,1.5) Alloys

Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy

Microstructural characteristics and mechanical properties of cast Al-3Li-xCu-0.2Zr alloy

Effects of magnesium and copper additions on tensile properties of Al-Si-Cr die casting alloy under as-cast and T5 conditions

Effect of Cu addition on microstructures and tensile properties of high-pressure die-casting Al-5.5Mg-0.7Mn alloy

Effect of Cooling Rate on Microstructure and Mechanical Properties of an Al-5.0Mg-3.0Zn-1.0Cu Cast Alloy

Effect of composition on the microstructure and mechanical properties of Mg-Al-Zn alloys

Investigating the role of Cu, Zr and V on the evolution of microstructure and properties of Al-Si-Mg cast alloys