Abstract:In consolidation of AlON, the extensive decomposition of AlON into α-Al2O3 and AlN during sintering is one of the major reasons that significantly retard its densification process. To accelerate densification of AlON, an ultra-low concentration of La2O3 (0.03 wt%) and Y2O3 (0.02-0.04 wt%) was co-doped as sintering additives to inhibit decomposition of AlON during sintering for fast fabrication of highly transparent AlON ceramics. The phase transformation, microstructure evolution and densification process of the samples undoped and doped additive during heating were studied to investigate the densification mechanism. The results reveal that, compared to the samples undoped additive and single-doped with La2O3, the α-Al2O3 content of the samples co-doped with La2O3 and Y2O3 is significantly deduced at ≤1600 °C, which indicates that the decomposition of AlON is effectively inhibited by co-doping La2O3 and Y2O3. The reduction of α-Al2O3 along with the deceleration effect of La3+ on mass transfer, contributes to more small particles being conserved at high temperatures. Base on this, at later stage of sintering, benefiting from the enhanced mobility of grain boundary by Y3+, AlON ceramics with high relative density (99.79 %) and excellent transparency were obtained via pressureless sintering at 1880 °C for 2.5 h by co-doping 0.03 wt% La2O3 and 0.04 wt% Y2O3. The maximum transmittance of the fabricated AlON ceramics is up to 81.6 % at 3600 nm, and a transmittance of 76.0 % was measured at 400 nm. The ultra-low doping amount of La2O3 and Y2O3 and the high relative density should be the main reasons that lead to the outstanding transparency of the obtained AlON. Additionally, the fabricated AlON ceramics also exhibit a high Vickers hardness of 18.89 ± 0.18 GPa.

Highly oriented α-Al2O3 transparent ceramics shaped by shear force

High transmittance and grain-orientated alumina ceramics fabricated by adding fine template particles

Plastic Deformation and Sintering of Alumina under High Pressure

Porous Alumina Ceramics with Unidirectional Oriented Pores Fabricated by Ionotropic Process of Sodium Alginate

Preparation and properties of porous alumina with highly ordered and unidirectional oriented pores by a self-organization process

Mechanical and Optical Properties of Transparent Alumina Obtained by Rapid Vacuum Sintering

The hydrolysis process of γ-AlON powder and preparation of highly transparent ceramics with aqueous gel-casting

Influence of Particle Size and Aggregates on Translucent Alumina Ceramics Fabricated by Gelcasting

Two-step pressureless sintering of ultrafine powders for the preparation of high strength and transmittance AlON ceramics

Al2O3 Ceramics with Well-Oriented and Hexagonally Ordered Pores: the Formation of Microstructures and the Control of Properties

Fabrication of transparent alumina by rapid vacuum pressureless sintering technology

Alumina assisted grain refinement and physical performance enhancement of yttria transparent ceramics by two-step sintering

Direct coarse powder aqueous slip casting and pressureless sintering of highly transparent AlON ceramics

Progress in sintering technology of transparent polycrystalline alumina ceramics

Ultrafast high-temperature sintering of dense and textured alumina

Improved Fracture Behavior and Mechanical Properties of Alumina Textured Ceramics

Fabrication of highly transparent AlON ceramics by inhibiting decomposition of AlON

Highly Transparent Alumina Spark Plasma Sintered from Common-Grade Commercial Powder: the Effect of Powder Treatment

Preparation and optical properties of highly transparent MgAl1.9Ga0.1O4 ceramics via aqueous gel-casting method

Hierarchically porous Al2TiO5 ceramics via freeze-gel casting

Fabrication and properties of highly transparent Li0.07Al2.76O3.64N0.36 ceramics by aqueous gelcasting and two-step preparation