Abstract:High crystallization, low-dielectric-loss Li2O-xMgO-ZnO-B2O3-SiO2 x = 30, 35, 40, 45 and 50 wt.%) (LMZBS) glass-ceramics were prepared with different MgO contents using the solid-state method in this study. The effects of the MgO content on the microstructures, flexural strength and microwave dielectric properties of LMZBS were investigated. X-ray diffractometer results, for samples sintered at 920 degrees C, for 30 wt.% <= x <= 35 wt.%, showed that the main phase was Mg2B2O5 and the secondary phase was Li2ZnSiO4. But a new Mg3B2O6 phase appeared when the MgO content exceeded 35 wt.%, becoming the main phase at x = 50 wt.%. Scanning electron microscopy showed that the average grain size decreased with increases in MgO and that a compact, homogeneous microstructure could be obtained at x = 40 wt.%. The Q x f value product of qualify factor and resonant frequency) increased at first due to increases in the theoretical Q quality factor) value and relative density, and then decreased due to a decrease in the average grain size and the appearance of large amounts of the liquid phase. Finally, the Li2O-xMgO-ZnO-B2O3-SiO2 glass-ceramics with 40 wt.% MgO exhibited excellent microwave properties and mechanical properties in terms of dielectric constants (epsilon(r) = 6.66), Qxf = 54600 GHz, temperature coefficient of resonant frequency (tau(f) = (1) 35 ppm/degrees C) and flexural strength (sigma = 160MPa) after the samples were sintered at 920 degrees C for 2 h in air, indicating their suitability as low-temperature co-fired ceramics. (C) 2018 The Ceramic Society of Japan. All rights reserved.

Effect of Zn 2? substitution for Mg 2? in Li 3 Mg 2 SbO 6 and the impact on the bond characteristics and microwave dielectric properties

Effect of Zn2+ substitution for Mg2+ in Li3Mg2SbO6 and the impact on the bond characteristics and microwave dielectric properties

Effect of Sb-site nonstoichiometry on the structure and microwave dielectric properties of Li 3 Mg 2 Sb 1− x O 6 ceramics

Effect of Sb-site nonstoichiometry on the structure and microwave dielectric properties of Li3Mg2Sb1−xO6 ceramics

Effects of Cu2+substitution on bond characteristics, Raman spectra, and microwave dielectric properties of Li2Mg0.6Zn0.4SiO4 ceramics

Effects of Zn2+ Substitution on the Sintering Behaviour and Dielectric Properties of Li2Mg1−xZnxSiO4 Ceramics

Effect of zirconium deficiency on structure characteristics, morphology and microwave dielectric properties of Li2Mg3Zr1-xO6 ceramics

Phase evolution, structure and microwave dielectric properties of Li2+xMg3SnO6 (x = 0.00–0.12) ceramics

Bond Characteristics And Microwave Dielectric Properties Of High-Q Materials In Li-Doped Zn3b2o6 Systems

Synthesis, Phase Composition and Modified Microwave Dielectric Properties of Mg2+ Substituted Zn2SiO4 Ceramics with Uniform Microstructure

High sintering and dielectric performance: The improved (Mg, Zn)3B2O6 ceramics with the help of the DFT calculation

Effects of Mg2+ Substitution on Microstructure and Microwave Dielectric Properties of (zn1−xmgx)nb2o6 Ceramics

Microwave dielectric properties of Li 2 O– x MgO–ZnO–B 2 O 3 –SiO 2 glass-ceramics ( x = 30–50 wt.%)

Influence of Li<sub>2</sub>O-MgO-ZnO-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub>glass doping on the microwave dielectric properties and sintering temperature of Li<sub>3</sub>Mg<sub>2</sub>NbO<sub>6</sub>ceramics

Effects of Li-ion substitution on the microwave dielectric properties of low-temperature sintered ceramics with nominal composition Li2xMg2−xSiO4

Microstructure and Microwave Dielectric Properties of (zn1−xmgx)2sio4 Ceramics

Microwave dielectric properties of Li<sub>2</sub>O–<i>x</i>MgO–ZnO–B<sub>2</sub>O<sub>3</sub>–SiO<sub>2</sub> glass-ceramics (<i>x</i> = 30–50 wt.%)

Zn-modified Li3Mg2SbO6 Microwave Dielectric Ceramics with High-Quality Factor

Effect of Mg/B ratio and Sr2+ substitution for Mg2+ on the sintering, phase composition and microwave dielectric properties of Mg3B2O6 ceramics

Effects of Li 2 ZnTi 3 O 8 Addition on Sintering Behavior and Microwave Dielectric Properties of the MgTiO 3 –catio 3 Ceramic System

Effect of Cation Occupancy on Crystal Structure and Microwave Dielectric Characteristics of Spinel-Structured (1-X)zn2tio4-xli2mgti3o8 Ceramics