Abstract:Ni-MgO dual function materials (DFMs) show promise for integrated CO2 sorption and methanation. To improve CO2 sorption capacity, Ni-MgO DFMs are promoted with alkali metal nitrates. However, the high catalyst reduction temperature will result in high energy consumption, huge temperature gap between reduction (similar to 650 degrees C) and CO2 sorption and methanation (similar to 300 degrees C), and the loss of alkali metal nitrates. In this work, we prepared a Ni/CeO2 catalyst and investigated the effect of reduction temperature on its structure-property relationships in CO2 methanation, aiming to lower the reduction temperature to an isothermal level that matches CO2 methanation. Results indicated that the reduction temperature fell from over 650 to 300 degrees C, and Ni/CeO2 reduced at 300 degrees C featured high CO2 conversion (72.7%) and CH4 selectivity (98.9%). The CO2 methanation activity of Ni/CeO2 declined significantly when the reduction temperature exceeded 400 degrees C. The formation of more oxygen vacancy defects due to the interaction between NiO and CeO2 promoted the reduction of NiO species at lower temperatures. The declined CO2 methanation activity at high reduction temperatures was ascribed to the consumption of oxygen vacancies in catalyst reduction, and less defects were available for CO2 activation and methanation. An alkali metal nitrate promoted MgO adsorbent was physically mixed with Ni/CeO2 to construct (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs for integrated CO2 sorption and methanation. The DFMs could be facilely reduced at 300 degrees C, and this has made it possible to realize the isothermal operation of catalyst reduction and CO2 sorption and methanation in integrated CO2 capture and utilization (ICCU). The (Li-Na-K)NO3-MgO-Ni/CeO2-phy DFMs reduced at 300 degrees C exhibited an impressive CO2 uptake of 2.74 mmol CO2/g DFMs and a great CH4 yield of 1.10 mmol CH4/g DFMs, and they could be a promising alternative to Ru-based DFMs with respect to their comparable CO2 sorption capacity and methanation activity and minimized cost of raw materials.

Influence of doping Mg cation in Fe3O4 lattice on its oxygen storage capacity to use as a catalyst for reducing emissions of a compression ignition engine

Insights into Nickel-Based Dual Function Materials for CO2 Sorption and Methanation: Effect of Reduction Temperature

Influence of the Chemical Composition of MgAlFeCu Mixed Oxides As Catalysts for SO2Removal

Influence of different Fe doping strategies on modulating active sites and oxygen reduction reaction performance of Fe, N-doped carbonaceous catalysts

Doped Mn modulates the local charge distribution of cobalt-based spinel catalysts to promote the availability of ligand lattice oxygen for complete oxidation of methane

Enhancement of magnesium aluminate-based nickel and cobalt nanostructured catalysts with iron for improved performance in carbon dioxide methanation

Mn Doping at High‐Activity Octahedral Vacancies of γ‐Fe2O3 for Oxygen Reduction Reaction Electrocatalysis in Metal‐Air Batteries

Insight to structure-activity relationship of non-stoichiometric CuMgAl spinel catalysts for CO hydrogenation to dimethyl ether: Effect of MgO doping amount

A systematic evaluation of the catalytic behavior of transition metal (Fe and Mn)–doped ceria-zirconia-alumina oxides on automobile exhaust

The performance of an atomically dispersed oxygen reduction catalyst prepared by γ-CD-MOF integration with FePc

Promotional Effects of Sm/Ce/La Doping on Soot Oxidation over MnCo2O4 Spinel Catalysts

In-situ Metal Doping to Boost the Reactivity of Layered Double Hydroxide Derived Mg-Fe-Al-O Oxygen Carriers for Chemical Looping CH4 Reforming with CO2 Reduction

Enhancing CO catalytic oxidation performance over Cu-doping manganese oxide octahedral molecular sieves catalyst

O-Doping Boosts the Electrochemical Oxygen Reduction Activity of a Single Fe Site in Hydrophilic Carbon with Deep Mesopores

Doping Manganese Oxides with Ceria and Ceria Zirconia Using a One-Pot Sol–Gel Method for Low Temperature Diesel Oxidation Catalysts

Fe, N-doped carbon spheres prepared by electrospinning method as high efficiency oxygen reduction catalyst

Metal-oxygen bonding nanoarchitectonics for regulation of oxygen evolution reaction performance in FeNi-codoped CoOOH

Activating Inert Sites in Cobalt Silicate Hydroxides for Oxygen Evolution through Atomically Doping

Effect of Mn-dopant on carburization of the Fe3O4 catalysts in Fischer-Tropsch synthesis

DFT insights into doping and oxygen vacancy effects on CO and CO2 adsorptions over CuAl 2 O 4 spinel surfaces

Revealing the intrinsic nature of Cu- and Ce-doped Mn3O4 catalysts with positive and negative effects on CO oxidation using operando DRIFTS-MS