Abstract:Granulation serves as an effective strategy for mitigating the elutriation of CaO-based sorbents in the fluidized bed-based Calcium Looping system designed for CO 2 capture. Here, hydrophobic interface-assisted casted CaO-based sorbent pellets were prepared via a range of hydrophobic materials, i.e., graphite, Nano-titanium dioxide, Nano-silica, and polyethylene powders. The contact Angle values of the composite slurry droplets for the four hydrophobic materials range from 126 to 143°, which can provide enough surface tension to form CaO-based sorbent pellets. Moreover, the Al-based stabilizer precursors in the form of oxide, nitrate and sol, respectively, were incorporated into CaO-based pellets aiming to enhance their cyclic CO 2 uptake stability. Soluble aluminum nitrate exhibits the superior performance on enhancing CO 2 uptake stability compared to Nano-alumina and alumina sol, whose superiority lies in its ability to disperse more evenly with the active CaO component. Therefore, the Al-supported CaO-based pellet (∼30 wt% of Ca 12 Al 14 O 33 ) with aluminum nitrate as the precursor of Al-based stabilizer remains excellent CaO carbonation conversion of 50.3 % after 20 cycles, approximately 2 times that of pure CaO pellet. Even under harsh calcination condition (950 °C, 100 vol% CO 2 ), the Al-supported CaO-based pellet is still markedly superior to CaO pellet for cyclic CO 2 capture. The freshly calcined Al-supported CaO-based pellet exhibits highly desirable compressive strength (3.4 ± 0.83 MPa), compared to 0.35 ± 0.07 MPa for pure CaO pellet. The generated inert Ca 12 Al 14 O 33 skeleton provides structural stability and strength to the Al-supported, CaO-based pellets, which simultaneously contributes to the enhanced cyclic CO 2 uptake capacity and mechanical property.

Microemulsion-derived, nanostructured CaO/CuO composites with controllable particle grain size to enhance cyclic CO2 capture performance for combined Ca/Cu looping process

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

Facile fabrication of aluminum-oxide deposited CuO/CaO composites with enhanced stability and CO2 capture capacity for combined Ca/Cu looping process

Morphological Changes of Pure Micro‐ and Nano‐Sized CaCO3 during a Calcium Looping Cycle for CO2 Capture

Synthesis And Characterization Of Cao Nanopods For High Temperature Co2 Capture

Stabilizer-coated combined Ca/Cu pellets with controllable particle sizes for the Ca/Cu chemical loop

Core-shell structured CaO-based pellets with enhanced cyclic CO2 capture performance

Wet Mixing Combustion Synthesis of CaO-based Sorbents for High Temperature Cyclic CO2 Capture

Synthesis and Performance of a Nano Synthetic Ca-based Sorbent for High Temperature CO_2 Capture

Achieving simultaneous Cu particles anchoring in meso-porous TiO2 nanofabrication for enhancing photo-catalytic CO2 reduction through rapid charge separation

Reactivity and Microstructure of Synthetic CaO-based Sorbents for CO2 Capture

Development of Highly Effective CaO@Al2O3 with Hierarchical Architecture CO2 Sorbents Via a Scalable Limited-Space Chemical Vapor Deposition Technique

Hydrophobic interface-assisted casting of Al-supported, CaO-based sorbent pellets for high-temperature CO 2 capture

Enhancing Calcium Oxide-Based Carbon Capture Cycles with Ion-Doped Spinels

Core‐shell structured CaO‐based pellets protected by mesoporous ceramics shells for high‐temperature CO2 capture

Self-reactivated mesostructured Ca-Al-O composite for enhanced high-temperature CO2 capture and carbonation/calcination cycles performance.

High-performance CaO-based Composites Synthesized Using a Space-Confined Chemical Vapor Deposition Strategy for Thermochemical Energy Storage

Novel synthetic sol–gel CaO based pellets using porous mesostructured silica in cyclic CO 2 capture process

A Facile fabrication of mesoporous core–shell CaO-Based pellets with enhanced reactive stability and resistance to attrition in cyclic CO2 capture

Size Effect of Calcium Precursor and Binder on CO2 Capture of Composite CaO-based Pellets

Enhancement of Mixing and Mass Transfer Performance with a Microstructure Minireactor for Controllable Preparation of CaCO3 Nanoparticles