Hydrophobic interface-assisted casting of Al-supported, CaO-based sorbent pellets for high-temperature CO 2 capture
Yuxuan Zhang,Jian Sun,Long Jiang,Xiaoyu Zhang,Chuanwen Zhao,Changsheng Bu
DOI: https://doi.org/10.1016/j.seppur.2024.126797
IF: 8.6
2024-02-20
Separation and Purification Technology
Abstract:Granulation serves as an effective strategy for mitigating the elutriation of CaO-based sorbents in the fluidized bed-based Calcium Looping system designed for CO 2 capture. Here, hydrophobic interface-assisted casted CaO-based sorbent pellets were prepared via a range of hydrophobic materials, i.e., graphite, Nano-titanium dioxide, Nano-silica, and polyethylene powders. The contact Angle values of the composite slurry droplets for the four hydrophobic materials range from 126 to 143°, which can provide enough surface tension to form CaO-based sorbent pellets. Moreover, the Al-based stabilizer precursors in the form of oxide, nitrate and sol, respectively, were incorporated into CaO-based pellets aiming to enhance their cyclic CO 2 uptake stability. Soluble aluminum nitrate exhibits the superior performance on enhancing CO 2 uptake stability compared to Nano-alumina and alumina sol, whose superiority lies in its ability to disperse more evenly with the active CaO component. Therefore, the Al-supported CaO-based pellet (∼30 wt% of Ca 12 Al 14 O 33 ) with aluminum nitrate as the precursor of Al-based stabilizer remains excellent CaO carbonation conversion of 50.3 % after 20 cycles, approximately 2 times that of pure CaO pellet. Even under harsh calcination condition (950 °C, 100 vol% CO 2 ), the Al-supported CaO-based pellet is still markedly superior to CaO pellet for cyclic CO 2 capture. The freshly calcined Al-supported CaO-based pellet exhibits highly desirable compressive strength (3.4 ± 0.83 MPa), compared to 0.35 ± 0.07 MPa for pure CaO pellet. The generated inert Ca 12 Al 14 O 33 skeleton provides structural stability and strength to the Al-supported, CaO-based pellets, which simultaneously contributes to the enhanced cyclic CO 2 uptake capacity and mechanical property.
engineering, chemical