Precursor Infiltration and Pyrolysis Cycle-Dependent Mechanical and Microwave Absorption Performances of Continuous Carbon Fibers-Reinforced Boron-Containing Phenolic Resins for Low-Density Carbon-Carbon Composites

Yu Sun,Yuguo Sun

DOI: https://doi.org/10.1016/j.ceramint.2020.03.053

IF: 5.532

2020-01-01

Ceramics International

Abstract:Low-density C/C composites with continuous carbon fiber-reinforced boron-containing phenolic resin (B-containing PR) were successfully prepared through a simple precursor infiltration and pyrolysis process (PIP), the influence of PIP cycle numbers ranging from 1 to 4 on the microstructure, thermal conductivity, mechanical and microwave absorption properties of as-prepared C/C composites were investigated in detail for the first time. The results shown that the microstructure, thermal conductivity, mechanical and microwave absorption properties of as-prepared C/C composites strongly depended on the PIP cycle numbers. The bulk densities of the C/C composites increased as the number of PIP cycles increased, and the open porosities of the samples decreased with the increase of PIP cycle numbers. The compressive strengths and thermal conductivities of the C/C composites were remarkably strengthened as the number of PIP cycle increased. The electromagnetic wave (EMW) absorption performances of C/C composites with different PIP cycle numbers were investigated, and the minimal reflection loss (RLmin) value and the maximum effective absorption bandwidth (EAB) value of as-prepared C/C samples was -10.5 dB and 0.94 GHz (9.22-10.16 GHz) under the optimization condition for S2 sample with two PIP cycle numbers. The difference of EMW absorption properties among as-prepared C/C composites was analyzed in detail from the two important evaluation indicators, namely the characteristic impedance and attenuation constant, and present study implies that a relative balance between impedance matching and the attenuation constant should be considered for achieving the best EMW absorption performance.