Abstract:Enhancing the fire safety of epoxy resins (EPs) typically requires a significant amount of flame retardants, which often results in considerable degradation of their mechanical properties. To address this issue, a novel flame retardant known as PDCP@DPA@MXene was synthesized and integrated into EP to achieve notable improvements in flame retardancy, smoke suppression, and mechanical strength. By incorporating 1.5 wt% PDCP@DPA@MXene, the impact strength, tensile strength, and elongation at break of the resulting PDM-1.5 %/EP composite reached 12.1 kJ/m2, 57.4 MPa, and 13.0, respectively, reflecting enhancements of 63.5 %, 18.4 %, and 17.1 % compared to the pure EP. The enhancement in tensile strength may be attributed to the high rigidity of Ti3C2Tx MXene, which reinforces the EP matrix. Additionally, the intertwined structure of PDCP@DPA@MXene chains effectively mitigates material fracturing and absorbs impact forces, thus toughening the EP. The presence of phosphorus, nitrogen, and titanate in PDCP@DPA@MXene contributes to the formation of a more compact char layer. The PDM-1.5 %/EP sample achieved a V-0 rating in the vertical UL-94 test and exhibited a high limiting oxygen index of 32.0. Furthermore, the sample containing 2 wt% PDCP@DPA@MXene showed a significant reduction in peak heat release rate (p-HRR) and total heat release (THR), recording values of 689 kW/m2 and 71.9 MJ/m2, which are decreases of 45.1 % and 26.9 %, respectively, compared to pure EP. Additionally, the incorporation of PDCP@DPA@MXene led to a reduction in CO production. These flame-retarded EPs demonstrate strong potential for various applications due to their elevated glass transition temperature and robust thermal stability.

Metal-organic Framework@polyaniline Nanoarchitecture for Improved Fire Safety and Mechanical Performance of Epoxy Resin

Hybridization of the Zinc-Based Organic Framework with Diphenylfenosundinyl Chloride and Its Combination with Hexaphenoxycyclotriphosphazene for Flame Retardancy of Epoxy Resin

Hierarchical MoS 2 /polyaniline binary hybrids with high performance for improving fire safety of epoxy resin

A Novel Co(Ⅱ)–based Metal-Organic Framework with Phosphorus-Containing Structure: Build for Enhancing Fire Safety of Epoxy

Designing 3D ternary-structure based on SnO2 nanoparticles anchored hollow polypyrrole microspheres interconnected with N, S co-doped graphene towards high-performance polymer composite

A novel P, N doped organic-inorganic hierarchical core-shell nanostructures: Reducing the fire risk of epoxy resin

High fire-safety epoxy resin with functional polymer/metal–organic framework hybrids

Hydrogen bonding induced polyphosphazene/MXenes 2D/2D structure loaded with MOFs enabling fire-safe epoxy composite

1/2D SnO2 Nanowires on MnO2 Nanosheets Hybrid Architecture for Reducing Fire Hazards of Epoxy Nanocomposites

Heterolayered Boron Nitride/Polyaniline/Molybdenum Disulfide Nanosheets for Flame-Retardant Epoxy Resins

Synthesis of MnO 2 Nanoparticles with Different Morphologies and Application for Improving the Fire Safety of Epoxy

Linear polydichlorophosphazene and Ti3C2Tx MXene nanohybrids: Synthesis and application to epoxy resin to improve the fire safety and mechanical properties

MOFs-based core-shell micro-nanostructure covering with curly RGO nanoflakes enabled fire-safe and mechanical-robust EP composites

Novel Phosphorus-Nitrogen-Containing Ionic Liquid Modified Metal-Organic Framework as an Effective Flame Retardant for Epoxy Resin

Fire-safe epoxy composite realized by MXenes based nanostructure with vertically arrayed MOFs derived from interfacial assembly strategy

A Facile Approach to Prepare Phosphorus and Nitrogen Containing Macromolecular Covalent Organic Nanosheets for Enhancing Flame Retardancy and Mechanical Property of Epoxy Resin

Construction of Nanomaterials Based on Molybdenum Disulfide Decorated onto a Metal–Organic Framework (UiO-66) to Improve the Fire Retardancy of Epoxy

Controllable dimensions and regular geometric architectures from self-assembly of lithium-containing polyhedral oligomeric silsesquioxane: Build for enhancing the fire safety of epoxy resin

Integrated Effect of Flame Retardant Wrapped Macromolecular Covalent Organic Nanosheet on Reduction of Fire Hazards of Epoxy Resin

Biomimetic construction of hierarchical MXene@PDA@CoFeOx nanohybrids towards efficient fire-safe epoxy nanocomposites with enhanced thermal conductivity and mechanical properties

Polyaniline‐coupled graphene/nickel hydroxide nanohybrids as flame retardant and smoke suppressant for epoxy composites