Abstract:Enhancing the fire safety of epoxy resins (EPs) typically requires a significant amount of flame retardants, which often results in considerable degradation of their mechanical properties. To address this issue, a novel flame retardant known as PDCP@DPA@MXene was synthesized and integrated into EP to achieve notable improvements in flame retardancy, smoke suppression, and mechanical strength. By incorporating 1.5 wt% PDCP@DPA@MXene, the impact strength, tensile strength, and elongation at break of the resulting PDM-1.5 %/EP composite reached 12.1 kJ/m2, 57.4 MPa, and 13.0, respectively, reflecting enhancements of 63.5 %, 18.4 %, and 17.1 % compared to the pure EP. The enhancement in tensile strength may be attributed to the high rigidity of Ti3C2Tx MXene, which reinforces the EP matrix. Additionally, the intertwined structure of PDCP@DPA@MXene chains effectively mitigates material fracturing and absorbs impact forces, thus toughening the EP. The presence of phosphorus, nitrogen, and titanate in PDCP@DPA@MXene contributes to the formation of a more compact char layer. The PDM-1.5 %/EP sample achieved a V-0 rating in the vertical UL-94 test and exhibited a high limiting oxygen index of 32.0. Furthermore, the sample containing 2 wt% PDCP@DPA@MXene showed a significant reduction in peak heat release rate (p-HRR) and total heat release (THR), recording values of 689 kW/m2 and 71.9 MJ/m2, which are decreases of 45.1 % and 26.9 %, respectively, compared to pure EP. Additionally, the incorporation of PDCP@DPA@MXene led to a reduction in CO production. These flame-retarded EPs demonstrate strong potential for various applications due to their elevated glass transition temperature and robust thermal stability.

Hydrogen bonding induced polyphosphazene/MXenes 2D/2D structure loaded with MOFs enabling fire-safe epoxy composite

Hybridization of the Zinc-Based Organic Framework with Diphenylfenosundinyl Chloride and Its Combination with Hexaphenoxycyclotriphosphazene for Flame Retardancy of Epoxy Resin

Fire-safe epoxy composite realized by MXenes based nanostructure with vertically arrayed MOFs derived from interfacial assembly strategy

Organic-inorganic Hybrid Engineering MXene Derivatives for Fire Resistant Epoxy Resins with Superior Smoke Suppression

Linear polydichlorophosphazene and Ti3C2Tx MXene nanohybrids: Synthesis and application to epoxy resin to improve the fire safety and mechanical properties

Surface modification of MXene nanosheets with P-N-containing agents for boosting flame retardancy of epoxy resin

In-situ encapsulated MXene nanosheets with bimetallic phosphate: towards for reducing the fire risk of epoxy composites

Interface Engineering of MXene Towards Highly Fire-Safe Epoxy Resin with Enhanced Thermal Conductivity

Fabrication of layered double hydroxide@ferric decorated polyphosphazene hybrid architecture towards simultaneously improved fire safety, smoke suppression and mechanical strength of epoxy resin

Novel Phosphorus-Nitrogen-Containing Ionic Liquid Modified Metal-Organic Framework as an Effective Flame Retardant for Epoxy Resin

Facile Strategy to Synthesize MXene@LDH Nanohybrids for Boosting the Flame Retardancy and Smoke Suppression Properties of Epoxy

Construction of Polyphosphazene-Functionalized Ti3c2tx with High Efficient Flame Retardancy for Epoxy and Its Synergetic Mechanisms

Precise Control of a Yolk-Double Shell Metal-Organic Framework-Based Nanostructure Provides Enhanced Fire Safety for Epoxy Nanocomposites

Novel design of MOFs-based hierarchical nanoarchitecture: Towards reducing fire hazards of epoxy resin

Co-based Metal-Organic Framework with Phosphonate and Triazole Structures for Enhancing Fire Retardancy of Epoxy Resin

Rationally Assembled Sandwich Structure of MXene-based Phosphorous Flame Retardant at Ultra-Low Loading Nanosheets Enabling Fire-Safe Thermoplastic Polyurethane

Hierarchical Polyphosphazene@Molybdenum Disulfide Hybrid Structure for Enhancing the Flame Retardancy and Mechanical Property of Epoxy Resins

Assembling MXene with bio-phytic acid: Improving the fire safety and comprehensive properties of epoxy resin

Biomimetic construction of hierarchical MXene@PDA@CoFeOx nanohybrids towards efficient fire-safe epoxy nanocomposites with enhanced thermal conductivity and mechanical properties

3D MXene Frameworks for Flame Retardant Hydrophobic Polymer Nanocomposites

MOFs-based core-shell micro-nanostructure covering with curly RGO nanoflakes enabled fire-safe and mechanical-robust EP composites