Hierarchical Porous Nanosilica Derived from Coal Gasification Fly Ash with Excellent CO2 Adsorption Performance
Yanfang Liu,Zhiqiang Wang,Wenhui Zhao,Jili Hou,Longpeng Cui,Liang Zou,Chenghao Li,Hongwei Li,Yu Wu,Run Xu,Yongfa Zhu
DOI: https://doi.org/10.1016/j.cej.2022.140622
IF: 15.1
2023-01-01
Chemical Engineering Journal
Abstract:The preparation of mesoporous silica from solid waste is an effective method to realize high-value utilization of solid waste and reduce the synthesis cost of mesoporous silica. However, the silica derived from solid waste often suffers from small pore size and weak adsorption capacity. Besides, the traditional method of extracting silicon from solid waste requires high-temperature melting in the presence of a large amount of alkali, resulting in equipment corrosion. In this work, hierarchical porous nanosilica was prepared via microwave-assisted alkaline extraction followed by hydrothermal synthesis, using coal gasification fly ash (CGFA) as silicon source. The microwave assisted alkali-dissolution process is fast in silicon extraction and induces less impurity metal ions. Besides, the Fixed Carbon in CGFA was degraded into C20H24O3, C5H10O and C16H35NO3. These compounds acted as swelling agent, inducing intergranular pores with sizes greater than 10 nm in the nanosilicas. The isosteric heat of adsorption of the hierarchical porous nanosilica was-30.06 kJ/mol, indicating that CO2 was adsorbed by the hierarchical porous nanosilica via both physisorption and chemisorption. Chemisorption was induced by the surface silanol and its density increased with the intergranular pores. Because the intergranular pores and surface silanol group provided more adsorption sites, the CO2 adsorption capacity of the hierarchical porous nanosilica was significantly improved, which reached 1.63 mmol/g at 30 celcius and 1 bar.