Abstract:The hot roll bending patchwork components of B1500HS uncoated ultra-high strength steel processed at industrial scale were welded with filler wire. The microstructure, grain orientation, mechanical properties and fracture behavior of the joint were investigated. The results showed that the weld metal (WM) was mainly composed of lath martensite and lower bainite (LB). Various microstructure appeared in different positions of the HAZ, among which martensite-austenite (M-A) constituents in the incompletely quenched zone and tempered martensite (TM) in the tempered zone were the key factors determining the performance of the joint. The welded joint exhibited complex structure and anisotropic mechanical response due to the decarburization and rolling texture of the original base material (BM). In the tempered zone, lath merge and boundaries disappear lead to the annihilation of dislocations, carbide precipitation leads to reduction of mobile dislocations, and recrystallization and recovery eliminate work hardening. The reduction of the effect of dislocation strengthening results in the formation of a softening belt at 6 mm from the center of the weld, with a minimum hardness of 266 HV. The tensile strength of the joint in the rolling direction (RD) was 983 MPa, and the fracture occurred in the softening belt. Both brittle and ductile fracture features were observed. The reason why the fracture occurs in the high temperature tempered zone instead of the incompletely quenched zone was the difference in the effect of "constraint strengthening". Fracture occurred through delamination cracking along the "weak interface" owing to precipitated high-hardness cementite particles and the unfavorably oriented ferrite cleavage planes.

Microstructure Evolution and Mechanical Properties of W/MA956 Joints by Brazing

Investigation of tungsten/MA956 steel diffusion bonding with an Nb/Ni composite interlayer

Microstructure and Mechanical Properties of Diffusion Bonded W/MA956 Steel Joints with a Titanium Interlayer by SPS

Microstructure and Properties of Brazed W-W Joints by Ti-35Ni Alloy

Microstructural evolution and mechanical properties of Ni-based superalloy joints brazed using a ternary Ni-W-B amorphous brazing filler metal

Interfacial Microstructure and Mechanical Properties of TZM Alloy and ZrC Particle Reinforced Tungsten Composite Joint Brazed Using Ti-61Ni Filler

Interfacial Microstructure and Properties of TZM Alloy and ZrCp-W Composite Joints Brazed Using Ti-50Ni Filler

Brazing Oxide Dispersion-Strengthened Fe-Based Steels with a Cu-Based Filler Metal

Metallurgical and Mechanical Investigations of Aluminium-Steel Butt Joint Made by Tungsten Inert Gas Welding–brazing

Microstructural evolution and mechanical properties in the self-propagating brazing joint of Al 0.1 CoCrFeNi HEAs and 304 SS using reactive multilayer nanofoils

Microstructure and mechanical properties of cemented carbide to steel joints by electron beam welding

Microstructure and Joint Properties of High-Nitrogen Steel Brazed by AgCuNi Filler Metal

Interfacial Microstructure and Mechanical Properties of TZM Alloy Joints Brazed Using Ti-28Ni Filler Metal

Interfacial Microstructure and Mechanical Properties of TZM Alloy Joints Vacuum Brazed Using Ti-Zr-Ni-Cu Filler Metal

Investigating the Effect of WC Reinforcements in Cu Ti Composite Filler on the Microstructural Evolution and Mechanical Characteristics in Brazing Cf/SiC and GH3536

Microstructure and Mechanical Properties of TIG Brazing of Stainless Steel

Microstructure and Mechanical Performance of Dissimilar Metal Joints of Aluminium Alloy and Stainless Steel by Cutting-Assisted Welding-Brazing

Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

Insights into microstructure evolution and fracture mechanisms of welded joints of high strength steel patchwork components

Investigations of the microstructure and mechanical properties of the Nb-Ti/Nb-Ti-Ni brazed joints

Investigating the effect of WC reinforcements in Cu Ti composite filler on the microstructural evolution and mechanical characteristics in brazing C f /SiC and GH3536