Abstract:Metallographic analysis techniques such as optical microscopy and scanning electron microscopy were used to observe the morphology of spline wear, confirming the presence of fretting wear characteristics. Microstructural analysis of spline cross sections using a metallographic microscope revealed surface carburization treatment on the splines. Hardness tests conducted from the surface to the core of the splines showed a gradual decrease in hardness, consistent with the observed microstructural features. The chemical composition of the spline was analyzed using a spectrometer, and the main component content was analyzed. By combining finite element analysis techniques, this study analyzed the effects of factors such as forces, eccentricity, and lubrication on spline wear. The results indicated that the varying degrees of spline wear in the hydraulic motors of charging pumps in the on-site conditions of the nuclear power plant were primarily attributed to differences in spline eccentricity after manufacture and assembly. Further investigation revealed that the fundamental cause of spline wear in hydraulic motors was the operation of the equipment under conditions deviating from the rated operating points, resulting in poor circulation of oil within the motors and insufficient spline lubrication. Specifically, operating the equipment at lower pressures and away from the rated operating points resulted in reduced oil flow velocity, increasing the friction between the spline mating surfaces. The poor lubrication of the spline and eccentricity are the primary reasons for spline wear, and the combination of these two factors exacerbates spline wear. To address the wear issue of the hydraulic motor, we replaced it with a linear-axis hydraulic motor and conducted a comprehensive analysis of the linear-axis hydraulic motor. The results indicate that the linear-axis hydraulic motor can effectively reduce wear, and after testing at the nuclear power plant, it meets the operational time requirements on-site. These findings offer valuable guidance for the maintenance and operation of charging pumps in nuclear power plants, facilitating the prevention of similar issues and enhancing equipment reliability and operational efficiency.

Analysis of the Causes of Driving Gear Shaft Fractures in Gear Pumps

Fracture failure analysis of transmission gear shaft in a bidirectional gear pump

Lubrication Performance Analysis of Fuel Gear Pump Sliding Bearing under High Speed and Wide Temperature Range

High Cycle Fatigue Failure with Radial Cracks in Gears of Aero-Engines

Failure analysis and structural fatigue resistance design of multistage centrifugal pump shaft

Analysis of Bearing Failures in a Typical High-Power Marine Gearbox

Experimental and Numerical Studies on Erosion Damage in Damping Holes on the Valve Plate of an Axial Piston Pump

Experimental and Numerical Study of the Influence of Loading Direction on the Lubrication and Cooling of Self-Circulating Oil Bearing System Applied in Internal Gear Pumps

Finite element analysis and structural design of fracturing pump valve chamber under multiple working conditions

Research on Influence Factor and Mechanism of Gear Fracture

A method for gear fatigue life prediction considering the internal flow field of the gear pump

Modeling and Analysis of External Gear Pump Broken Tooth Failure Mechanism

Investigation on the Failure of the Gear Shaft Connected to Extruder

Fracture Analysis on Gear Shaft in Vulcanizer Tire Foundation

Analysis of Contact Stress and Fatigue Crack Growth of Transmission Shaft

Cause Analysis and Countermeasure on Premature Failure of a Driven Gear for the High-Speed Train

Investigation on bending fatigue failure of a micro-gear through finite element analysis

Study on High Performance Driving P/M Gear for Engine

Failure analysis and factors influencing spline wear in hydraulic motors of charging pumps in nuclear power plants

Wear performance analysis and simulation of external gear pump

Failure modes, mechanisms and causes of shafts in mechanical equipment