Abstract:Al-Ti-B intermediate alloys are widely used as grain refiners in aluminum alloys owing to the presence of Al3Ti and TiB2 phases. However, the existence of Zr in aluminum alloy melts often results in coarse grain size, leading to Al-Ti-B failure called Zr poisoning. There are three kinds of poisoning mechanisms related to TiB2, Al3Ti, and a combination of TiB2 and Al3Ti for Zr. First, Zr forms ZrB2 or Ti2Zr with TiB2 in Al-Ti-B to reduce the nucleation ability. Second, Zr existing in the aluminum melt with a high melting point Al3Zr then attracts Ti to reduce the dispersion of Ti as a growth inhibitor. Third, Zr reacts with Al3Ti on TiB2 surface to form Al3Zr, thereby increasing the degree of mismatch with Al and diminishing the refiner’s ability as a nucleation substrate. To gain a better understanding of the mechanism of Zr poisoning, the first principle was used in this study to calculate the adhesion works (ZrB2//Al3Ti), (Ti2Zr//Al3Ti), (Al3Zr//Al3Ti), (Al3Ti//Al), (TiB2//Al3Zr), and (Al3Zr//Al), as well as the surface energy of Al3Zr and adsorption energies of Al to Al3Ti or Al3Zr. The results demonstrated that Zr poisoning originated from the second guess. Zr element exiting in aluminum melt led to the formation of an Al3Zr (001) surface. The interfacial adhesion work of Al3Zr (001)//Al3Ti (001) was not weaker than that of TiB2//Al3Ti. As a result, Al3Zr first combined with Al3Ti to significantly decline the adsorption of Al3Ti (001) on Al, losing its role as a nucleating agent and grain coarsening. Overall, to prevent failure of the grain refiner in Zr containing aluminum melt, the adhesion work interface between the generated phase of the grain refiner and Al3Zr must remain lower to avoid the combination of the generated phase of grain refiner with Al3Zr. In sum, these findings look promising for evaluating future effects of grain refinement in Zr containing aluminum melt.

Mechanism of Sc Poisoning of Al-5Ti-1B Grain Refiner

Effect of Scandium on Grain refinement mechanism and Mechanical Properties of Al-7Si-0.6Mg alloy at Different Cooling Rates

In Situ Radiographic Study of the Grain Refining Behavior of Al3Sc During the Solidification of Al-10Cu Alloy

In situ radiographic study of the grain refining behavior of Al3Sc during the solidification of Al-1OCu alloy

Mechanism of Zr Poisoning Al-5Ti-B Grain Refiners Based on the First-Principles Calculation

Influence of minor Sc additions on grain refinement and microstructure characteristics of a high Zn-containing Al-Zn-Mg-Cu-Zr alloy

An experimental study of the effect of Ag, Cu, Li, Mg, Ni, Ti, Sc, Zr on grain refining in binary and multicomponent Al-based alloys

Effect of scandium on microstructure and mechanical properties of high zinc concentration aluminum alloys

Boosting the grain refinement of commercial Al alloys by compound addition of Sc

Research on Grain Refinement of Sc and Zr Addition in an Al-Mg-Zn Alloy from Experiments and First-Principles Calculations

Microstructure and Mechanical Properties of Al–Si–Mg–Cu–Ti Alloy with Trace Amounts of Scandium

Understanding grain refinement of Sc addition in a Zr containing Al-Zn-Mg-Cu aluminum alloy from experiments and first-principles

Effects of Sc Addition on the Microstructure and Mechanical Properties of Cast Al-3Li-1.5Cu-0.15Zr Alloy

Effect of Sc and Zr on Microstructure and Mechanical Properties of As‐Cast Al–Li–Cu Alloys

The Effects of Scandium Heterogeneous Distribution on the Precipitation Behavior of Al3(Sc, Zr) in Aluminum Alloys

Scandium (sc) Behavior in High Temperature Ti Alloys

Insights into Poisoning Mechanism of Zr by First Principle Calculation on Adhesion Work and Adsorption Energy between TiB2, Al3Ti, and Al3Zr

Modification Mechanism And Growth Process Of Al-3(Sc, Zr) Particles In As-Cast Al-Si-Mg-Cu-Zr-Sc Alloy

Discontinuous Precipitation of Nano-Al3Sc Particles in Al-Sc Alloy and Its Effect on Mechanical Property

Intermetallic Growth and Interfacial Properties of the Grain Refiners in Al Alloys

Effect of Sc microalloying on microstructure evolution and mechanical properties of extruded Al-Zn-Mg-Cu alloys