Abstract:The production of cement releases an enormous amount of CO2 into the environment. Besides, industrial wastes like silica fume and fly ash need effective utilization to reduce their impacts on the environment. This research aims to explore the influence of silica fume (SF) and fly ash (FA) individually and combine them as binary cementitious material (BCM) on the hardened properties and embodied carbon of roller compacted concrete (RCC). A total of ten mixes were prepared with 1:2:4 mix ratio at the different water-cement ratios to keep the zero slump of roller compacted concrete. However, the replacement proportions for SF were 5%–15%, and FA were 5%–15% by the weight of cement individually and combine in roller compacted concrete for determining the hardened properties and embodied carbon. In this regard, several numbers of concrete specimens (cubes and cylinders) were cast and cured for 7 and 28 days correspondingly. It was observed that the compressive strength of RCC is boosted by 33.6 MPa and 30.6 MPa while using 10% of cement replaced with SF and FA individually at 28 days, respectively. Similarly, the splitting tensile strength of RCC is enhanced by 3.5 MPa at 10% cement replaced with SF and FA on 28 days, respectively. The compressive and splitting tensile strength of RCC is increased by 34.2 MPa and 3.8 MPa at SF7.5FA7.5 as BCM after 28 days consistently. In addition, the water absorption of RCC decreased while using SF and FA as cementitious material individually and together at 28 days. Besides, the embodied carbon of RCC decreased with increasing the replacement level of SF and FA by the mass of cement individually and combined.

The mechanical property and frost resistance of roller compacted concrete by mixing silica fume and limestone powder: Experimental study

Mechanical and Durability Properties of Sustainable Self-Compacting Concrete with Recycled Concrete Aggregate and Fly Ash, Slag and Silica Fume

Development of Sustainable Self-Compacting Concrete Using Recycled Concrete Aggregate and Fly Ash, Slag, Silica Fume

Effect of silica fume and limestone powder on crack resistance property for roller compacted concrete

Influence of Limestone Powder and Fly Ash on the Freezing and Thawing Resistance of Roller-Compacted Concrete

Experimental study on strength and abrasion-resistance enhancement admixture

Experimental investigation on the effect of coarse aggregate size and silica fume dosage to the fracture parameters of concrete

Investigating on the Pavement Performance of Multi-Source Solid Wastes by Cement and Fly Ash

Rheological Behavior and Microstructure Characteristics of SCC Incorporating Metakaolin and Silica Fume

Effect of silica fume and fly ash as cementitious material on hardened properties and embodied carbon of roller compacted concrete

Fresh and Mechanical Properties of Self-Consolidating Concrete Incorporating Silica Fume and Metakaolin

Study of mechanization and mechanical property of cement mortar added with fly ash in case of early frost

Experimental study of RCC mixed with magnesia

Comparative Study on the Effects of Rice Husk Ash and Silica Fume on the Freezing Resistance of Metakaolin-Based Geopolymer

Fineness Influence of Cement on Mechanical Properties of RCC

Freeze-Thaw Resistance and Microstructural Analysis of Recycled Aggregate Concrete Incorporating Ferronickel Slag As Fine Aggregate

Mechanical properties and micro-structure analysis of concrete adding high performance composite cementious material

Frost Resistance and Microscopic Properties of Recycled Coarse Aggregate Concrete Containing Chemical Admixtures

Experimental Research on Frost-resistance of Concrete with Adding of MgO

Sustainable ultra-high performance concrete with incorporating mineral admixtures: Workability, mechanical property and durability under freeze-thaw cycles

Production of Roller Compacted Concrete Made of Recycled Asphalt Pavement Aggregate and Recycled Concrete Aggregate and Silica Fume